Technical specifications of American high temperature alloy AM-355 Round bar, Flat bar, Forgings , S35500 ESR melted, Hot rolling, Heat treatment
TECHNICAL DATA SHEET - AM-355 & S35500
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Austenitic high-tensile superalloy & Precipitation hardening steel
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.10 ~ 0.15
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 0.50 ~ 1.25
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 15.0 ~ 16.0
Nickel, Ni (％): 4.00 ~ 5.00
Molybdenum, Mo (％): 2.50 ~ 3.20
Manganese, Mn (％): 0.50 ~ 1.25
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 15.0 ~ 16.0
Nickel, Ni (％): 4.00 ~ 5.00
Molybdenum, Mo (％): 2.50 ~ 3.20
Nb + Ta (%): 0.15 ~ 0.50
Nitrogen, N (%): -
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Tensile strength, Rm ≥ MPa: 1170
Yield strength, Rp0.2 ≥ MPa: 1070
Elonghation, A5 ≥(％): 12.0
Reduction of area, Z ≥ (％): 25.0
Hardness | HB: HRC37
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged.
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged.
FORMS AND DIMENSIONS
Round bar (Diameter): 5.5mm to 800mm
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, and other different shapes based on OEM.
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts, and other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search：AM-355/S35500
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1