Specifications 29Cr-7Ni-2Mo-N Austenite-Ferrite S32906 Round bar, Flat bar, Forging Bar Plate S32906 ESR & VAR technique, Hot blooming, Hot forging, Hot rolling, Heat treatment.
TECHNICAL DATA SHEET - UNS S32906
MATERIAL CATEGORY - 29Cr-7Ni-2Mo-N Austenite-Ferrite type.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the softened condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the softened condition.
Final heat treatment - solution treatment / QT
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): ≤ 0.030
Carbon, C (%): ≤ 0.030
Silicon, Si (%): ≤ 0.50
Manganese, Mn (%): 0.80 ~ 1.50
Phosphorus, P (%)≤: 0.030
Sulfur, S (%)≤: 0.030
Chromium, Cr (%): 28.0 ~ 30.0
Nickel, Ni (%): 5.80 ~ 7.50
Molybdenum, Mo (%): 1.50 ~ 2.60
Nitrogen, N (%): 0.30 ~ 0.40
Copper, Cu (%): ≤ 0.80
Manganese, Mn (%): 0.80 ~ 1.50
Phosphorus, P (%)≤: 0.030
Sulfur, S (%)≤: 0.030
Chromium, Cr (%): 28.0 ~ 30.0
Nickel, Ni (%): 5.80 ~ 7.50
Molybdenum, Mo (%): 1.50 ~ 2.60
Nitrogen, N (%): 0.30 ~ 0.40
Copper, Cu (%): ≤ 0.80
Form: sheet,strip, bar
Condition: annealing
Tensile strength, σb/MPa: 750
Yield strength, σ0.2/MPa: 550
Elongation, δ (%): 25.0
Elongation, δ (%): 25.0
Reduction of area, ф(%): -
Hardness | HRC(HBW): 310 max.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 400mm
Square bar / Flat bar: 10mm to 600mm
Plate / Sheet steel / Steel strip: 0.5mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
Square bar / Flat bar: 10mm to 600mm
Plate / Sheet steel / Steel strip: 0.5mm to 1000mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. Email: sales@ccsteels.com
Hot search:S32906
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1