Material Specification NF A36-209 Stainless Steel Z3CN18-10 Round bar, Flat bar 3CN18-10 Sheet, Steelmaking, ESR melting, Hot forging/rolling, Heat treatment.
TECHNICAL DATASHEET - Grade NF Z3CN18-10
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Stainless Steel plate for boiler and pressure vessel
Technical standards: NF A36-209 - 1992
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.030
Silicon, Si (％): ≤ 0.75
Manganese, Mn (％): ≤ 2.00
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.010
Chromium, Cr (％): 17.0 ~ 19.0
Phosphorus, P (％)≤: 0.040
Sulfur, S (％)≤: 0.010
Chromium, Cr (％): 17.0 ~ 19.0
Molybdenum, Mo (％): -
Nickel, Ni (%): 9.00 ~ 11.0
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength,σb/≥ MPa: 550 ~ 650
Yield strength, σ0.2/≥ MPa: 200
Elongation, δ ≥(％): 45.0
Yield strength, σ0.2/≥ MPa: 200
Elongation, δ ≥(％): 45.0
Reduction of area, (%): 45.0
Annealed hardness, HB ≤: 215
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / EF / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment
The alloy is usually produced by AOD / EF / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment
ADVANTAGED STOCK
High alloy and superalloy for turbine blade
ASTM A565 Grade 616/422/S42200, Grade 615/S41800, XM-32/S64152
17-4PH/630/1.4542, 631, 851, 961, WB36, D6-AC, D6A.
1.4980, 1.4922, 1.4923, 1.4935, 1.4938, 1.4913
Forms: Bars, Forge piece, Ring, Strip
Non-magnetic alloy
X40MnCrN19/1.3813, X8CrMnN18-18/1.3816, X40MnCr18/1.3817, N1310
Forms: Bars, Forge piece, Ring, Strip.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, you can EMAIL our qualified production engineers, E-mail: sales@ccsteels.com.
If you meet further on any technical enquiry, you can EMAIL our qualified production engineers, E-mail: sales@ccsteels.com.
Hot search：Z3CN18-10
Previous page：SAE T8 / T12008
Last page：Z3CN18-10Az
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1