1Cr12W1MoV
2017-09-13 11:33:13 Origin： Remark：0 Click：
Specifications 1Cr12W1MoV Heat Resisting Steel, Round bar Flat bar 1Cr12WMoV Stock Available, ESR melting, Hot forging, Hot rolling, Heat treatment
TECHNICAL DATASHEET - Grade 1Cr12W1MoV
Technical standards: GB/T 8732 - 2014 & GB/T 1221-2007
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.12 ~ 0.18
Silicon, Si (％): ≤ 0.50
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.12 ~ 0.18
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 0.50 ~ 0.90
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 11.0 ~ 13.0
Phosphorus, P (％) ≤: 0.035
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 11.0 ~ 13.0
Molybdenum, Mo (％): 0.50 ~ 0.70
Nickel, Ni (%): 0.40 ~ 0.80
Nitrogen, N (%): -
Vanadium, V (%): 0.15 ~ 0.30
Tungsten, W (%): 0.70 ~ 1.10
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength,σb/≥ MPa: 735
Yield strength, σ0.2/≥ MPa: 585
Elongation, δ ≥(％): 15.0
Yield strength, σ0.2/≥ MPa: 585
Elongation, δ ≥(％): 15.0
Reduction of area, (%): 45.0
QT treated hardness, HB ≤: 241 ~ 285
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / EF / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered + SRA.
The alloy is usually produced by AOD / EF / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered + SRA.
ADVANTAGED STOCK
High alloy and superalloy for turbine blade
ASTM A565 Grade 616/422/S42200, Grade 615/S41800, XM-32/S64152
17-4PH/630/1.4542, 631, 851, 961, WB36, D6-AC, D6A.
1.4980, 1.4922, 1.4923, 1.4935, 1.4938, 1.4913
Forms: Bars, Forge piece, Ring, Strip
Non-magnetic alloy
X40MnCrN19 / 1.3813, X8CrMnN18-18 / 1.3816, X40MnCr18 / 1.3817, N1310
Forms: Bars, Forge piece, Ring, Strip.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, you can do as follows:
EMAIL our qualified production engineers, E-mail: sales@ccsteels.com
If you meet further on any technical enquiry, you can do as follows:
EMAIL our qualified production engineers, E-mail: sales@ccsteels.com
Hot search：1Cr12W1MoV
Previous page：2Cr12MoVNbN
Last page：2Cr12NiMo1W1V
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1