1Cr12Ni2W1Mo1V
2017-09-15 11:41:51 Origin： Remark：0 Click：
Description 1Cr12Ni2W1Mo1V Ex-stock, Inventory 1Cr12Ni2W1Mo1V Suppliers, 1Cr12Ni2W1Mo1V Forgings properties from Steelmaking, ESR melting, Hot blooming, UT, Hot forging, Hot rolling, Heat treat, Straightening, 100% Ultrasonic test, Cold working or Machined. Technical specifications - GB/T 8732 - 2014. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATASHEET - Grade 1Cr12Ni2W1Mo1V & Grade 851
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Heat resisting Steel for Turbine blade
MATERIAL CATEGORY: Heat resisting Steel for Turbine blade
Technical standards: GB/T 20878-2007 & GB/T 8732 - 2014
CHEMICAL COMPOSITION (Mass weight - %)
C (％): 0.11 ~ 0.16
Si (％): 0.10 ~ 0.35
CHEMICAL COMPOSITION (Mass weight - %)
C (％): 0.11 ~ 0.16
Si (％): 0.10 ~ 0.35
Mn (％): 0.40 ~ 0.80
P (％)≤: 0.025
S (％)≤: 0.020
Cr (％): 10.5 ~ 12.5
P (％)≤: 0.025
S (％)≤: 0.020
Cr (％): 10.5 ~ 12.5
Mo (％): 1.00 ~ 1.40
Ni (%): 2.20 ~ 2.50
V (%): 0.15 ~ 0.35
W (%): 1.00 ~ 1.40
Al (%): ≤ 0.05
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength,σb/≥ MPa: 920
Yield strength, σ0.2/≥ MPa: 735
Elongation, δ ≥(％): 13.0
Yield strength, σ0.2/≥ MPa: 735
Elongation, δ ≥(％): 13.0
Reduction of area, (%): 40.0
Impact, AKv/J ≥: 48
QT hardness, HB ≤: 277 ~ 331
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / EF / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment
The alloy is usually produced by AOD / EF / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment
ADVANTAGED STOCK
High alloy and superalloy for turbine blade:
ASTM A565 Grade 616/422/S42200, Grade 615/S41800, XM-32/S64152.
17-4PH/630/1.4542, 631, 851, 961, WB36, D6AC, D6A..
1.4980, 1.4922, 1.4923, 1.4935, 1.4938, 1.4913.
Forms: Bars, Forge piece, Ring, Strip.
Non-magnetic alloy.
X40MnCrN19/1.3813, X8CrMnN18-18/1.3816, X40MnCr18/1.3817, N1310.
Forms: Bars, Forge piece, Ring, Strip.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, you can do as follows:
EMAIL our qualified production engineers.
If you meet further on any technical enquiry, you can do as follows:
EMAIL our qualified production engineers.
E-mail: sales@ccsteels.com
Hot search：1Cr12Ni2W1Mo1V
Previous page：665H20 / AISI 4620
Last page：1Cr12Ni2WMoVNb
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1