1Cr11Ni2W2MoV
2017-09-16 09:15:32 Origin： Remark：0 Click：
Round bar 1Cr11Ni2W2MoV Inventory, GJB 2294-95 Specifications 1Cr11Ni2W2MoV Forging, Plate ESR melting, Hot blooming, UT, Hot forging, Heat treated.
MATERIAL TECHNICAL DATA SHEET - Grade 1Cr11Ni2W2MoV
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Heat resisting Steel for Turbine blade
MATERIAL CATEGORY: Heat resisting Steel for Turbine blade
Technical standards: GB/T 20878-2007 & GB/T 8732 - 2014 & GJB - 2294
Inventory & Stocklist - Round bar diameter 20 ~ 250mm
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.10 ~ 0.16
Silicon, Si (％): ≤ 0.60
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.10 ~ 0.16
Silicon, Si (％): ≤ 0.60
Manganese, Mn (％): ≤ 0.60
Phosphorus, P (％)≤: 0.030
Sulfur, S (％)≤: 0.015
Chromium, Cr (％): 10.5 ~ 12.0
Phosphorus, P (％)≤: 0.030
Sulfur, S (％)≤: 0.015
Chromium, Cr (％): 10.5 ~ 12.0
Molybdenum, Mo (％): 0.35 ~ 0.50
Nickel, Ni (%): 1.40 ~ 1.80
Vanadium, V (%): 0.18 ~ 0.30
Tungsten, W (%): 1.50 ~ 2.00
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Contion: QT1 (Tempering 660 ~ 710 Deg. C)
Tensile strength,σb/≥ MPa: 885
Yield strength, σ0.2/≥ MPa: 738
Elongation, δ ≥(％): 15.0
Yield strength, σ0.2/≥ MPa: 738
Elongation, δ ≥(％): 15.0
Reduction of area, (%): 55.0
Impact, AKu/J ≥: 71
QT hardness, HB ≤: 269 ~ 311
Contion: QT2 (Tempering 540 ~ 590 Deg.C)
Tensile strength,σb/≥ MPa: 1080
Yield strength, σ0.2/≥ MPa: 885
Elongation, δ ≥(％): 12.0
Yield strength, σ0.2/≥ MPa: 885
Elongation, δ ≥(％): 12.0
Reduction of area, (%): 50.0
Impact, AKv/J ≥: 55
QT hardness, HB ≤: 311 ~ 388
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment
The alloy is usually produced by AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment
ADVANTAGED STOCK
High alloy and superalloy for turbine blade
ASTM A565 Grade 616 /422 /S42200, Grade 615 /S41800, XM-32 /S64152
17-4PH/630/1.4542, 631, 851, 961, WB36, D6-AC, D6A.
1.4980, 1.4922, 1.4923, 1.4935, 1.4938, 1.4913
Forms: Bars, Forge piece, Ring, Strip
Non-magnetic alloy
X40MnCrN19/1.3813, X8CrMnN18-18/1.3816, X40MnCr18/1.3817, N1310
Forms: Bars, Forge piece, Ring, Strip.
ADVANTAGE & SUPERIOR SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Hot search：1Cr11Ni2W2MoV
Previous page：1Cr12Ni2WMoVNb
Last page：1Cr14Ni3W2VB
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1