1Cr14Ni3W2VB
2017-09-16 10:10:08 Origin： Remark：0 Click：
Material technical specifications QJ 501A -98 Heat resisting steel 1Cr14Ni3W2VB datasheet, Grade 1Cr14Ni3W2VB Chemical compositions, 1Cr14Ni3W2VB mechanical properties from Steel making, ESR melting, Hot blooming, UT, Grade 1Cr14Ni3W2VB Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or Machined. Technical specifications - QJ 501A -98. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL SPECIFICATION DATASHEET - Grade 1Cr14Ni3W2VB
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Heat resisting Steel for Turbine blade
MATERIAL CATEGORY: Heat resisting Steel for Turbine blade
Technical standards: GB/T 20878-2007 & QJ 501A -98
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.10 ~ 0.16
Si (％): ≤ 0.60
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.10 ~ 0.16
Si (％): ≤ 0.60
Mn (％): ≤ 0.60
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 13.0 ~ 15.0
P (％)≤: 0.030
S (％)≤: 0.030
Cr (％): 13.0 ~ 15.0
Mo (％): -
Ni (%): 2.80 ~ 3.40
V (%): 0.18 ~ 0.28
W (%): 1.60 ~ 2.20
Ti (%): ≤ 0.05
B (%): ≤ 0.004
MECHANICAL PROPERTIES
Contion: QT1 (Quenching 1040 ~ 1060 Deg, air/oil cooled, Tempering 600 ~ 680 Deg., air cooled.)
Tensile strength,σb/≥ MPa: 930
Yield strength, σ0.2/≥ MPa: 735
Elongation, δ ≥(％): 14.0
Yield strength, σ0.2/≥ MPa: 735
Elongation, δ ≥(％): 14.0
Reduction of area, (%): 55.0
Impact, AKu/J ≥: 70
QT hardness, HB ≤: -
Contion: QT2 (Quenching 1040 ~ 1060 Deg, air/oil cooled, Tempering 550 ~ 600 Deg., air cooled.)
Tensile strength,σb/≥ MPa: 1130
Yield strength, σ0.2/≥ MPa: 880
Elongation, δ ≥(％): 12.0
Yield strength, σ0.2/≥ MPa: 880
Elongation, δ ≥(％): 12.0
Reduction of area, (%): 50.0
Impact, AKv/J ≥: 55
QT hardness, HB ≤: -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / EF / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment
The alloy is usually produced by AOD / EF / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment
ADVANTAGED STOCK
High alloy and superalloy for turbine blade
ASTM A565 Grade 616/422/S42200, Grade 615/S41800, XM-32/S64152
17-4PH/630/1.4542, 631, 851, 961, WB36, D6-AC, D6A.
1.4980, 1.4922, 1.4923, 1.4935, 1.4938, 1.4913
Forms: Bars, Forge piece, Ring, Strip
Non-magnetic alloy
X40MnCrN19/1.3813, X8CrMnN18-18/1.3816, X40MnCr18/1.3817, N1310
Forms: Bars, Forge piece, Ring, Strip
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, you can do as follows:
EMAIL our qualified production engineers, E-mail: lh.steel@hotmail.com
Hot search：1Cr14Ni3W2VB
Previous page：1Cr11Ni2W2MoV
Last page：1Cr12Mo
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1