Martensitic Steel 1Cr12Mo Round bar, flat bar, 12Cr12Mo Forgings Stock Available, Steelmaking, ESR melting, Hot forging/rolling, Heat treatment
TECHNICAL DATA SHEET - 1Cr12Mo
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
Material category- Heat resisting Steel for Turbine blade
Material category- Heat resisting Steel for Turbine blade
Technical standards: GB/T 20878-2007 & GB/J 8732-2014
Stock Available: Round bar diam. 20 ~ 300mm, ESR ingot, Forging billet.
Flat bar / plate 10 ~ 200 * 15 ~ 600 * Lmm
Typical chemical compositions (mass fraction - %)
Carbon, C (％): 0.10 ~ 0.15
Silicon, Si (％): ≤ 0.50
Typical chemical compositions (mass fraction - %)
Carbon, C (％): 0.10 ~ 0.15
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 0.30 ~ 0.60
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.020
Chromium, Cr (％): 11.5 ~ 13.0
Phosphorus, P (％) ≤: 0.030
Sulfur, S (％) ≤: 0.020
Chromium, Cr (％): 11.5 ~ 13.0
Molybdenum, Mo (％): 0.30 ~ 0.60
Nickel, Ni (%): 0.30 ~ 0.60
Vanadium, V (%): -
Tungsten, W (%): -
Copper, Cu (%): ≤ 0.30
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: Q+T (Quenching 950 ~ 1000 Deg, oil cooled, Tempering 650 ~ 710 Deg., air cooled.)
Tensile strength, Rm ≥ MPa: 685
Yield strength, Rp 0.2 ≥ MPa: 550
Elongation, A5 ≥ (％): 18.0
Yield strength, Rp 0.2 ≥ MPa: 550
Elongation, A5 ≥ (％): 18.0
Reduction of area, Z (%): 60.0
Impact strength, AKv2 J ≥: 78
QT hardness, HB ≤: 217 ~ 255
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / EF / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered + SRA.
The alloy is usually produced by AOD / EF / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered + SRA.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, please do EMAIL our qualified production engineers or sales department, Email: sales@ccsteels.com.
If you meet further on any technical enquiry, please do EMAIL our qualified production engineers or sales department, Email: sales@ccsteels.com.
Hot search：1Cr12Mo
Previous page：1Cr14Ni3W2VB
Last page：1Cr11MoV
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1