NF A36-209 -1992 type Z3CND19-14Az is an Austenitic steel of alloy content 18Cr-13Ni-3Mo base, it is produced from Steelmaking, ESR melting, Hot blooming, UT, Hot forging, Hot rolling, Heat treatment, Cold machined.
TECHNICAL DATASHEET - Grade NF Z3CND19-14Az
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Stainless Steel plate for boiler and pressure vessel
Technical standards: NF A36-209 - 1992
CHEMICAL COMPOSITION (mass weight %)
C (％): ≤ 0.030
Si (％): ≤ 0.75
Mn (％): ≤ 2.00
P (％)≤: 0.035
S (％)≤: 0.010
Cr (％): 18.0 ~ 20.0
P (％)≤: 0.035
S (％)≤: 0.010
Cr (％): 18.0 ~ 20.0
Mo (％): 3.00 ~ 4.00
Ni (%): 13.0 ~ 15.0
N (%): 0.12 ~ 0.20
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, σb/≥ MPa: 550
Yield strength, σ0.2/≥ MPa: 240
Elongation, δ ≥(％): 40.0
Yield strength, σ0.2/≥ MPa: 240
Elongation, δ ≥(％): 40.0
Reduction of area, (%): -
Annealed hardness, HB ≤: 217
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / EF / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment
The alloy is usually produced by AOD / EF / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment
ADVANTAGED STOCK
High alloy and superalloy for turbine blade
ASTM A565 Grade 616/422/S42200, Grade 615/S41800, XM-32/S64152
17-4PH/630/1.4542, 631, 851, 961, WB36, D6-AC, D6A.
1.4980, 1.4922, 1.4923, 1.4935, 1.4938, 1.4913
Forms: Bars, Forge piece, Ring, Strip
Non-magnetic alloy
X40MnCrN19/1.3813, X8CrMnN18-18/1.3816, X40MnCr18/1.3817, N1310
Forms: Bars, Forge piece, Ring, Strip
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, you can do as follows:
EMAIL our qualified production engineers, E-mail: sales@ccsteels.com.
If you meet further on any technical enquiry, you can do as follows:
EMAIL our qualified production engineers, E-mail: sales@ccsteels.com.
Hot search：Z3CND19-14Az
Previous page：665M23
Last page：Duratherm 700
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1