N10276
2017-09-29 08:53:19 Origin： Remark：0 Click：
Specifications N10276 data sheet, N10276 Chemical, N10276 properties from Steelmaking, ESR melted, Blooming, Forging, Hot rolling, Heat treat, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - ASTM B564-04 Grade N10276
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: low-carbon-Ni-Mo-Cr Alloy
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.020
Si (％): ≤ 0.08
Mn (％): ≤ 1.00
P (％) ≤: 0.040
S (％) ≤: 0.030
Cr (％): 14.5 ~ 16.5
Ni (％): Remainder
Mo (％): 15.0 ~ 17.0
Cu (%): -
Mn (％): ≤ 1.00
P (％) ≤: 0.040
S (％) ≤: 0.030
Cr (％): 14.5 ~ 16.5
Ni (％): Remainder
Mo (％): 15.0 ~ 17.0
Cu (%): -
Al (%): -
Ti (%): -
Ce (%): -
Zr (%): -
Y (%): -
Nb (%): -
Co (%): ≤ 2.50
V (%): ≤ 0.35
N (%): -
B (%): -
W (%): 3.00 ~ 4.50
W (%): 3.00 ~ 4.50
Ta (%): -
Fe (%): 1.00 ~ 4.70
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: Solution annealed
Tensile strength, σb/≥ MPa: 690
Yield strength, σ0.2/≥ MPa: 283
Elonghation, δ ≥(％): 40.0
Fe (%): 1.00 ~ 4.70
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: Solution annealed
Tensile strength, σb/≥ MPa: 690
Yield strength, σ0.2/≥ MPa: 283
Elonghation, δ ≥(％): 40.0
Delivery hardness + A / HBW: -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
AVAILABLE FORMS AND SHAPES
Round bar (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T60 - 400mm X W70 - 1000mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
AVAILABLE FORMS AND SHAPES
Round bar (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 3mm to 500mm
Heavy/middle plate via hot rolled: T60 - 400mm X W70 - 1000mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W100 - 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：N10276
Previous page：Z3CND19-15-04
Last page：Z3CND22-05Az
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1