ASTM A564 Specifications S11100 Round bar, Flat bar, Forgings Steelmaking, ESR melted, Blooming, Hot forging, Hot rolling, Heat treatment
TECHNICAL DATA SHEET - ASTM A564 type S11100
TECHNICAL SPECIFICATION: ASTM A564 -2013
MATERIAL CATEGORY: Age-hardening stainless steel Alloy
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): ≤ 0.020
Carbon, C (％): ≤ 0.020
Silicon, Si (％): ≤ 0.25
Manganese, Mn (％): ≤ 0.25
Phosphorus, P (％) ≤: 0.015
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 10.25 ~ 11.25
Molybdenum, Mo (％): 1.75 ~ 2.25
Manganese, Mn (％): ≤ 0.25
Phosphorus, P (％) ≤: 0.015
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 10.25 ~ 11.25
Molybdenum, Mo (％): 1.75 ~ 2.25
Titanium, Ti (%): 0.20 ~ 0.50
Aluminum, Al (%): 1.35 ~ 1.75
Copper, Cu (%): -
Nitrogen, N (%): ≤ 0.01
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: Solution annealed
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: Solution annealed
Heat treatment: 840,+/-14 Deg. Oil or water cooled, hold FOR 8h min. at -73 Deg. air warm
Tensile strength, Rm ≥ MPa: -
Tensile strength, Rm ≥ MPa: -
Yield strength, Rp0.2 ≥ MPa: -
Elonghation, Z ≥ (％): -
Hardness: HB331 max.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND DIMENSIONS
Round bar / Rod / Disc (diameter): 5.5mm ~ 750mm
Square bar / Flat bar: 10 ~ 600mm
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND DIMENSIONS
Round bar / Rod / Disc (diameter): 5.5mm ~ 750mm
Square bar / Flat bar: 10 ~ 600mm
Steel wire: Diam.0.10 ~ 13.0mm in coil form
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to Email (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry, pleased to Email (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search：S11100
Previous page：AMS 6515 / Maraging 350
Last page：S10120
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1