Technical specifications of ASTM A564 Age-hardening stainless steels S10120 data sheet, S10120 Chemical compositions, S10120 mechanical properties from Steelmaking, ESR melted, Blooming, Forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - ASTM A564 Grade S10120
TECHNICAL SPECIFICATION: ASTM A564 -2013
MATERIAL CATEGORY: Age-hardening stainless steel Alloy
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.020
C (％): ≤ 0.020
Si (％): ≤ 0.25
Mn (％): ≤ 0.25
P (％) ≤: 0.015
S (％) ≤: 0.010
Cr (％): 11.0 ~ 12.5
Ni (％): 9.00 ~ 10.5
Mo (％): 1.75 ~ 2.25
Mn (％): ≤ 0.25
P (％) ≤: 0.015
S (％) ≤: 0.010
Cr (％): 11.0 ~ 12.5
Ni (％): 9.00 ~ 10.5
Mo (％): 1.75 ~ 2.25
Ti (%): 0.20 ~ 0.50
Al (%): 0.80 ~ 1.10
Cu (%): -
N (%): ≤ 0.01
MECHANICAL PROPERTIES
Condition: Solution annealed
MECHANICAL PROPERTIES
Condition: Solution annealed
Heat treatment: 840,+/-14 Deg. Cool rapidly below 32 Deg.
Tensile strength, σb/≥ MPa: -
Tensile strength, σb/≥ MPa: -
Yield strength, σ0.2/≥ MPa: -
Elonghation, δ ≥(％): -
Hardness: HB331 max.
Condition: Age treated + H950
Ageing treated: 510 Deg. X 4h, Air or oil cooled.
Tensile strength, σb/≥ MPa: 1400
Tensile strength, σb/≥ MPa: 1400
Yield strength, σ0.2/≥ MPa: 1300
Elonghation, δ ≥(％): 9.0
Hardness: HB448 min.
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND SHAPES
Round bar (Diameter): 0.20mm to 650mm
Square bar / Flat bar: 3mm to 500mm
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged or double aged
FORMS AND SHAPES
Round bar (Diameter): 0.20mm to 650mm
Square bar / Flat bar: 3mm to 500mm
Steel wire: Diam.0.10 ~ 16.0mm, in coil form
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers.
- Email: lh.steel@hotmail.com
Hot search：S10120
Previous page：S11100
Last page：AISI M46 / ASTM M46
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1