Material technical specifications of NF A36-209 -1992 Stainless steel Z6CND18-12-03 data sheet, Z6CND18-12-03 Chemical compositions, Z6CND18-12-03 mechanical properties from Steelmaking, ESR melting, Hot blooming, UT, Grade Z6CND18-12-03 Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test,Cold working or Machined. Technical specifications - NF A36-209 - 1992. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATASHEET - NF Z6CND18-12-03
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Stainless Steel plate for boiler and pressure vessel
Technical standards: NF A36-209 - 1992
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.06
Si (％): ≤ 0.75
Mn (％): ≤ 2.00
P (％)≤: 0.040
S (％)≤: 0.015
Cr (％): 16.5 ~ 18.5
P (％)≤: 0.040
S (％)≤: 0.015
Cr (％): 16.5 ~ 18.5
Mo (％): 2.25 ~ 2.75
Ni (%): 11.0 ~ 13.0
MECHANICAL PROPERTIES
Tensile strength, TS, σb/≥ MPa: 550
Yield strength, YS, σ0.2/≥ MPa: 205
Elongation, EL, δ ≥(％): 40.0
Yield strength, YS, σ0.2/≥ MPa: 205
Elongation, EL, δ ≥(％): 40.0
Reduction of area, RA, (%): -
Annealed hardness, HB ≤: 217
PRODUCT DESCRIPTION
The alloy is usually produced by IFF + AOD + VD /AOD / EF / EAF + VD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment
The alloy is usually produced by IFF + AOD + VD /AOD / EF / EAF + VD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment
ADVANTAGED STOCK
High alloy and superalloy for turbine blade
ASTM A565 Grade 616/422/S42200, Grade 615/S41800, XM-32/S64152
17-4PH/630/1.4542, 631, 851, 961, WB36, D6-AC, D6A.
1.4980, 1.4922, 1.4923, 1.4935, 1.4938, 1.4913
Forms: Bars, Forge piece, Ring, Strip
Non-magnetic alloy
X40MnCrN19/1.3813, X8CrMnN18-18/1.3816, X40MnCr18/1.3817, N1310
Forms: Bars, Forge piece, Ring, Strip
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, you can do as follows:
EMAIL our qualified production engineers, E-mail: lh.steel@hotmail.com
Hot search：Z6CND18-12-03
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1