Z3CT20
2017-11-20 13:55:35 Origin： Remark：0 Click：
Material technical specifications of NF A35-573 -1990 Stainless steel Z3CT20 data sheet, Z3CT20 Chemical compositions,Grade Z3CT20 mechanical properties from Steelmaking,ESR melting, Hot blooming, UT, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or Machined. Technical specifications - NF A36-209 - 1992. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATASHEET - NF Z3CT20
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Stainless Steel plate, steel strip
Technical standards: NF A35-573 - 1990
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.030
Si (％): ≤ 0.75
MATERIAL CATEGORY: Stainless Steel plate, steel strip
Technical standards: NF A35-573 - 1990
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.030
Si (％): ≤ 0.75
Mn (％): ≤ 0.80
P (％)≤: 0.030
S (％)≤: 0.015
Cr (％): 19.5 ~ 20.5
P (％)≤: 0.030
S (％)≤: 0.015
Cr (％): 19.5 ~ 20.5
Mo (％): -
Ni (%): -
Ti (%): 0.30 ~ 0.60
N (%): ≤ 0.035
MECHANICAL PROPERTIES
Tensile strength, TS, σb/≥ MPa: 380 ~ 560
Yield strength, YS, σ0.2/≥ MPa: 220
Elongation, EL, δ ≥(％): 25.0
Yield strength, YS, σ0.2/≥ MPa: 220
Elongation, EL, δ ≥(％): 25.0
Reduction of area, RA, (%): -
Annealed hardness, HB ≤: 215
PRODUCT DESCRIPTION
The alloy is usually produced by IFF + AOD + VD /AOD / EF / EAF + VD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment
The alloy is usually produced by IFF + AOD + VD /AOD / EF / EAF + VD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment
ADVANTAGED STOCK
ASTM A565 Grade 616/422/S42200, Grade 615/S41800, XM-32/S64152, PH13-8/XM-13/S13800
FV520B /1.4594, PH15-7Mo /632 (S15700), 15-5PH /XM-12 (S15500), 17-4PH/630/1.4542, 17-7PH /631 (S17700),
851, 961, WB36, D6-AC, D6A. A-286/660, AM-350 /633 (S35000), AM-355 /634 (S35500), Custom 450/XM-25(S45000)
1.4980, X22CrMoV12-1/1.4923, 1.4935, 1.4938, 1.4913
Forms: Bars, Forge piece, Ring, Strip
Non-magnetic alloy
X40MnCrN19/1.3813, X8CrMnN18-18/1.3816, X40MnCr18/1.3817, N1310, X55CrMnN18-4, X50MnCrV20-14, X5MnCrNiN18-13
DIN 1.3964, DIN 1.3974.
Forms: Bars, Forge piece, Ring
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, you can do as follows:
EMAIL our qualified production engineers.
If you meet further on any technical enquiry, you can do as follows:
EMAIL our qualified production engineers.
- E-mail: lh.steel@hotmail.com
Hot search：Z3CT20
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1