Material technical specifications of NF A35-573 -1990 Stainless steel NF Z6CN13-04 data sheet, Z6CN13-04 Chemical compositions, Z6CN13-04 mechanical properties from Steelmaking, ESR melting, Hot blooming, UT, Z6CN13-04 Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or Machined. Technical specifications - NF A36-209 - 1992. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATASHEET - NF Z6CN13-04
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Stainless Steel plate, steel strip
Technical standards: NF A35-573 - 1990
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.06
Si (％): ≤ 0.75
MATERIAL CATEGORY: Stainless Steel plate, steel strip
Technical standards: NF A35-573 - 1990
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.06
Si (％): ≤ 0.75
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.015
Cr (％): 12.0 ~ 13.5
P (％)≤: 0.040
S (％)≤: 0.015
Cr (％): 12.0 ~ 13.5
Mo (％): 0.30 ~ 0.50
Ni (%): 3.50 ~ 4.50
MECHANICAL PROPERTIES
Tensile strength, TS, σb/≥ MPa: 650 ~ 830
Yield strength, YS, σ0.2/≥ MPa: 520
Elongation, EL, δ ≥(％): 15.0
Yield strength, YS, σ0.2/≥ MPa: 520
Elongation, EL, δ ≥(％): 15.0
Reduction of area, RA, (%): -
Annealed hardness, HB ≤: -
PRODUCT DESCRIPTION
The alloy is usually produced by IFF + AOD + VD /AOD / EF / EAF + VD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment
The alloy is usually produced by IFF + AOD + VD /AOD / EF / EAF + VD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment
ADVANTAGED STOCK
AISI 690 /Refractaloy 26, ASTM A565 Grade 616 /422SS /S42200, Grade 615 /S41800, XM-32 /S64152, PH13-8 /XM-13 /S13800
FV520B /1.4594, PH15-7Mo /632 (S15700), 15-5PH /XM-12 (S15500), 17-4PH /630 /1.4542, 17-7PH /631 (S17700),
851, 961, WB36, D6-AC, D6A. A-286 /ASTM 660, AM-350 /633 (S35000), AM-355 /634 (S35500), Custom 450 /XM-25 (S45000)
1.4980, X22CrMoV12-1 /1.4923, 1.4935, 1.4938, 1.4913
Forms: Bars, Forge piece, Ring, Strip
Non-magnetic alloy
X40MnCrN19/1.3813, X8CrMnN18-18/1.3816, X40MnCr18/1.3817, N1310, X55CrMnN18-4, X50MnCrV20-14, X5MnCrNiN18-13
DIN 1.3964, DIN 1.3974, 23-8N /Nitronic 20,
Forms: Bars, Forge piece, Ring
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, you can do as follows:
EMAIL our qualified production engineers.
If you meet further on any technical enquiry, you can do as follows:
EMAIL our qualified production engineers.
- E-mail: lh.steel@hotmail.com
Hot search：Z6CN13-04
Previous page：820M17 / En354
Last page：BT42
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1