Description Z11CN17-08 Stocklist, Suppliers Z11CN17-08 Ex-stock, forgings Z11CN17-08 wire rod mechanical properties from Steelmaking, ESR melting, Hot blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or Machined. Technical specifications - NF A36-209 - 1992. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATASHEET - Grade NF Z11CN17-08
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Stainless Steel plate, steel strip
Technical standards: NF A35-573 - 1990
CHEMICAL COMPOSITION (Mass weight - %)
C (％): 0.09 ~ 0.12
Si (％): ≤ 0.75
MATERIAL CATEGORY: Stainless Steel plate, steel strip
Technical standards: NF A35-573 - 1990
CHEMICAL COMPOSITION (Mass weight - %)
C (％): 0.09 ~ 0.12
Si (％): ≤ 0.75
Mn (％): 0.75 ~ 1.20
P (％)≤: 0.040
S (％)≤: 0.015
Cr (％): 16.5 ~ 17.5
P (％)≤: 0.040
S (％)≤: 0.015
Cr (％): 16.5 ~ 17.5
Mo (％): -
Ni (%): 7.00 ~ 8.00
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, TS, σb/≥ MPa: 515
Yield strength, YS, σ0.2/≥ MPa: 205
Elongation, EL, δ ≥(％): 4 5.0
Yield strength, YS, σ0.2/≥ MPa: 205
Elongation, EL, δ ≥(％): 4 5.0
Reduction of area, RA, (%): -
Annealed hardness, HB ≤: 217
PRODUCT DESCRIPTION
The alloy is usually produced by IFF + AOD + VD /AOD / EF / EAF + VD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment
The alloy is usually produced by IFF + AOD + VD /AOD / EF / EAF + VD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment
ADVANTAGED STOCK
AISI 690 /Refractaloy 26, ASTM A565 Grade 616 /422SS /S42200, Grade 615 /S41800, XM-32 /S64152, PH13-8 /XM-13 /S13800
FV520B /1.4594, PH15-7Mo /632 (S15700), 15-5PH /XM-12 (S15500), 17-4PH /630 /1.4542, 17-7PH /631 (S17700),
851, 961, WB36, D6-AC, D6A. A-286 /ASTM 660, AM-350 /633 (S35000), AM-355 /634 (S35500), Custom 450 /XM-25 (S45000)
1.4980, X22CrMoV12-1 /1.4923, 1.4935, 1.4938, 1.4913
Forms: Bars, Forge piece, Ring, Strip
Non-magnetic alloy
X40MnCrN19/1.3813, X8CrMnN18-18/1.3816, X40MnCr18/1.3817, N1310, X55CrMnN18-4, X50MnCrV20-14, X5MnCrNiN18-13
DIN 1.3964, DIN 1.3974, 23-8N /Nitronic 20,
Forms: Bars, Forge piece, Ring.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, you can do as follows:
EMAIL our qualified production engineers, E-mail: sales@ccsteels.com.
If you meet further on any technical enquiry, you can do as follows:
EMAIL our qualified production engineers, E-mail: sales@ccsteels.com.
Hot search：Z11CN17-08
Previous page：Z10CNDA 15-07
Last page：STC 5
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1