Material technical specification of NF A35-573 -1990 Stainless steel Z44C14 datasheet,NF Z44C14 Chemical composition,Z44C14 mechanical properties from Steelmaking, ESR melting,Z44C14 Hot blooming, UT, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or Machined. Technical specifications - NF A36-209 - 1992. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATASHEET - NF Z44C14
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Stainless Steel plate, steel strip
Technical standards: NF A35-573 - 1990
CHEMICAL COMPOSITION (WEIGHT %)
C (%): 0.40 ~ 0.48
Si (%): ≤ 0.75
MATERIAL CATEGORY: Stainless Steel plate, steel strip
Technical standards: NF A35-573 - 1990
CHEMICAL COMPOSITION (WEIGHT %)
C (%): 0.40 ~ 0.48
Si (%): ≤ 0.75
Mn (%): ≤ 1.00
P (%)≤: 0.040
S (%)≤: 0.015
Cr (%): 12.5 ~ 14.0
S (%)≤: 0.015
Cr (%): 12.5 ~ 14.0
Mo (%): -
Ni (%): -
MECHANICAL PROPERTIES
Tensile strength, TS, σb/≥ MPa: 780 max.
Yield strength, YS, σ0.2/≥ MPa: -
Elongation, EL, δ ≥(%): 12.0
Yield strength, YS, σ0.2/≥ MPa: -
Elongation, EL, δ ≥(%): 12.0
Reduction of area, RA, (%): -
Annealed hardness, HB ≤: 245
PRODUCT DESCRIPTION
The alloy is usually produced by IFF + AOD + VD /AOD / EF / EAF + VD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment
The alloy is usually produced by IFF + AOD + VD /AOD / EF / EAF + VD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment
ADVANTAGED STOCK
AISI 690 /Refractaloy 26, ASTM A565 Grade 616 /422SS /S42200, Grade 615 /S41800, XM-32 /S64152, PH13-8 /XM-13 /S13800
FV520B /1.4594, PH15-7Mo /632 (S15700), 15-5PH /XM-12 (S15500), 17-4PH /630 /1.4542, 17-7PH /631 (S17700),
851, 961, WB36, D6-AC, D6A. A-286 /ASTM 660, AM-350 /633 (S35000), AM-355 /634 (S35500), Custom 450 /XM-25 (S45000)
1.4980, X22CrMoV12-1 /1.4923, 1.4935, 1.4938, 1.4913
Forms: Bars, Forge piece, Ring, Strip
Non-magnetic alloy
X40MnCrN19/1.3813, X8CrMnN18-18/1.3816, X40MnCr18/1.3817, N1310, X55CrMnN18-4, X50MnCrV20-14, X5MnCrNiN18-13
DIN 1.3964, DIN 1.3974, 23-8N /Nitronic 20,
Forms: Bars, Forge piece, Ring
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, you can do as follows:
EMAIL our qualified production engineers.
If you meet further on any technical enquiry, you can do as follows:
EMAIL our qualified production engineers.
- E-mail: lh.steel@hotmail.com
Hot search:Z44C14
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1