Material technical specifications of NF A35-573 -1990 Stainless steel Z5NCTDV25-15B datasheet, Z5NCTDV25-15B Chemical composition,Z5NCTDV25-15B mechanical properties from Steelmaking, ESR melting, Hot blooming, UT, Grade Z5NCTDV25-15B Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or Machined. Technical specifications - NF A36-209 - 1992. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATASHEET - NF Z5NCTDV25-15B
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Stainless Steel plate, steel strip
Technical standards: NF A35-573 - 1990
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.050
Si (％): ≤ 0.75
MATERIAL CATEGORY: Stainless Steel plate, steel strip
Technical standards: NF A35-573 - 1990
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.050
Si (％): ≤ 0.75
Mn (％): ≤ 2.00
P (％)≤: 0.030
S (％)≤: 0.015
Cr (％): 13.5 ~ 16.0
S (％)≤: 0.015
Cr (％): 13.5 ~ 16.0
Mo (％): 1.00 ~ 1.50
Ni (%): 24.0 ~ 27.0
V (%): 0.10 ~ 0.50
Ti (%): 1.80 ~ 2.30
B (%): 0.0025 ~ 0.0080
Al (%): ≤ 0.40
MECHANICAL PROPERTIES
| Test Temperature | Yield 0.2% | Yield 0.2% | Yield 0.2% | Yield 0.2% | Tensile Strength | % Elongation in 2" {50.8mm} | % Reduction of Area | |
|---|---|---|---|---|---|---|---|---|
| 0.2% offset | 0.2% offset | |||||||
| f/c | ksi | mpa | ksi | Mpa | ksi | Mpa | ||
| 70/21 | 90 | 621 | 92 | 655 | 145 | 1000 | 24 | 45 |
| 400/204 | 76 | 524 | 93 | 645 | 143 | 986 | 21 | 52 |
| 800/427 | 72 | 496 | 93 | 641 | 138 | 951 | 19 | 35 |
| 1000/538 | 62 | 427 | 87 | 603 | 131 | 903 | 18 | 31 |
| 1100/593 | 64 | 445 | 90 | 621 | 122 | 841 | 21 | 23 |
| 1200/649 | 62 | 431 | 88 | 607 | 103 | 713 | 13 | 14 |
| 1300/704 | 68 | 472 | 86 | 593 | 86 | 595 | 11 | 10 |
| 1400/760 | 44 | 307 | 62 | 427 | 64 | 441 | 18 | 23 |
| 1500/816 | ||||||||
PRODUCT DESCRIPTION
The alloy is usually produced by IFF + AOD + VD /AOD / EF / EAF + VD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment
The alloy is usually produced by IFF + AOD + VD /AOD / EF / EAF + VD followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment
ADVANTAGED STOCK
AISI 690 /Refractaloy 26, ASTM A565 Grade 616 /422SS /S42200, Grade 615 /S41800, XM-32 /S64152, PH13-8 /XM-13 /S13800
FV520B /1.4594, PH15-7Mo /632 (S15700), 15-5PH /XM-12 (S15500), 17-4PH /630 /1.4542, 17-7PH /631 (S17700),
851, 961, WB36, D6-AC, D6A. A-286 /ASTM 660, AM-350 /633 (S35000), AM-355 /634 (S35500), Custom 450 /XM-25 (S45000)
1.4980, X22CrMoV12-1 /1.4923, 1.4935, 1.4938, 1.4913
Forms: Bars, Forge piece, Ring, Strip
Non-magnetic alloy
X40MnCrN19/1.3813, X8CrMnN18-18/1.3816, X40MnCr18/1.3817, N1310, X55CrMnN18-4, X50MnCrV20-14, X5MnCrNiN18-13
DIN 1.3964, DIN 1.3974, 23-8N /Nitronic 20,
Forms: Bars, Forge piece, Ring
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, you can do as follows:
EMAIL our qualified production engineers.
If you meet further on any technical enquiry, you can do as follows:
EMAIL our qualified production engineers.
- E-mail: lh.steel@hotmail.com
Hot search：Z5NCTDV25-15B
Previous page：Z3CN17-11-01
Last page：Z8C17C1
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1