1.4534 / X3CrNiMoAl13-8-2
2018-04-25 14:09:55 Origin： Remark：0 Click：
Plate X3CrNiMoAl13-8-2 Ex-stock, Round bar 1.4534 flat bar X3CrNiMoAl13-8-2 Stock Available from Steelmaking, ESR melted, Hot forging/rolling, Heat treatment.
TECHNICAL DATA SHEET - DIN 1.4534 & X3CrNiMoAl13-8-2
MATERIAL CATEGORY: Martensitic precipitation hardening stainless steel
STOCK LIST & INVENTORY on Hand - Milled plate 41 X 650mm / 81 X 650mm
STOCK LIST & INVENTORY on Hand - Milled plate 41 X 650mm / 81 X 650mm
MELTING PROCESS - AOD / BEF / VIM + Consumable electrode remelted
HS code For Customs - 72201100 / 72202030 / 72221100 / 72222000 / 72223000
MAIN CHEMICAL ELEMENTS (mass weight - %)
HS code For Customs - 72201100 / 72202030 / 72221100 / 72222000 / 72223000
MAIN CHEMICAL ELEMENTS (mass weight - %)
Carbon, C (％): ≤ 0.05
Silicon, Si (％): ≤ 0.10
Manganese, Mn (％): ≤ 0.20
Phosphorus, P (％) ≤: 0.010
Sulfur, S (％) ≤: 0.008
Chromium, Cr (％): 12.3 ~ 13.2
Nickel, Ni (％): 7.50 ~ 8.50
Molybdenum, Mo (％): 2.00 ~ 2.50
Alumium (%): 0.90 ~ 1.35
Silicon, Si (％): ≤ 0.10
Manganese, Mn (％): ≤ 0.20
Phosphorus, P (％) ≤: 0.010
Sulfur, S (％) ≤: 0.008
Chromium, Cr (％): 12.3 ~ 13.2
Nickel, Ni (％): 7.50 ~ 8.50
Molybdenum, Mo (％): 2.00 ~ 2.50
Alumium (%): 0.90 ~ 1.35
Nitrogen (%): ≤ 0.01
MECHANICAL PROPERTIES UNDER DIFFERENT AGEING TEMPERATURES
Solution treatment temperature and cooling ways: 1050 +/-15℃
Ageing teated: H1000, 540℃, 4h, air cooling
Tensile strength, σb≥/MPa: 1410
Yield strength, σ0.2≥/MPa: 1312
Elongation, δ≥(％): 10.0
Hardness |HRC: 43
Ageing teated: H1025, 550℃, 4h, air cooling
Tensile strength, σb≥/MPa: 1275
Yield strength, σ0.2≥/MPa: 1200
Elongation, δ≥(％): 11.0
Hardness |HRC: 41
Ageing teated: H1050, 565℃, 4h, air cooling
Tensile strength, σb≥/MPa: 1200
Yield strength, σ0.2≥/MPa: 1135
Elongation, δ≥(％): 12.0
Hardness |HRC: 40
Ageing teated: H1100, 595℃, 4h, air cooling
Tensile strength, σb≥/MPa: 1030
Yield strength, σ0.2≥/MPa: 930
Elongation, δ≥(％): 14.0
Hardness |HRC: 34
Ageing teated: H1150, 620℃, 4h, air cooling
Tensile strength, σb≥/MPa: 930
Yield strength, σ0.2≥/MPa: 625
Elongation, δ≥(％): 14.0
Hardness |HRC: 30
PRODUCT DESCRIPTION
The alloy is usually produced by VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in solution annealed condition.
Final heat treatment - solution + ageing treated
TYPICAL APPLICATIONS
A high level of useful mechanical properties under severe environmental conditions. Alloy 13-8 Stainless Steel is used in aerospace components, landing gear, nuclear reactor components, petrochemical industry, injection molding equipment etc. Alloy 13-8 Stainless Steel in the annealed condition can be strengthened further by relatively low temperature heat treatment.
PRODUCT PROFILE & DIMENSIONS
Round bar / Disc (diameter): 5.50mm to 600mm
Square bar / Flat bar: 10mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Other different shapes based on OEM
MECHANICAL PROPERTIES UNDER DIFFERENT AGEING TEMPERATURES
Solution treatment temperature and cooling ways: 1050 +/-15℃
Ageing teated: H1000, 540℃, 4h, air cooling
Tensile strength, σb≥/MPa: 1410
Yield strength, σ0.2≥/MPa: 1312
Elongation, δ≥(％): 10.0
Hardness |HRC: 43
Ageing teated: H1025, 550℃, 4h, air cooling
Tensile strength, σb≥/MPa: 1275
Yield strength, σ0.2≥/MPa: 1200
Elongation, δ≥(％): 11.0
Hardness |HRC: 41
Ageing teated: H1050, 565℃, 4h, air cooling
Tensile strength, σb≥/MPa: 1200
Yield strength, σ0.2≥/MPa: 1135
Elongation, δ≥(％): 12.0
Hardness |HRC: 40
Ageing teated: H1100, 595℃, 4h, air cooling
Tensile strength, σb≥/MPa: 1030
Yield strength, σ0.2≥/MPa: 930
Elongation, δ≥(％): 14.0
Hardness |HRC: 34
Ageing teated: H1150, 620℃, 4h, air cooling
Tensile strength, σb≥/MPa: 930
Yield strength, σ0.2≥/MPa: 625
Elongation, δ≥(％): 14.0
Hardness |HRC: 30
PRODUCT DESCRIPTION
The alloy is usually produced by VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in solution annealed condition.
Final heat treatment - solution + ageing treated
TYPICAL APPLICATIONS
A high level of useful mechanical properties under severe environmental conditions. Alloy 13-8 Stainless Steel is used in aerospace components, landing gear, nuclear reactor components, petrochemical industry, injection molding equipment etc. Alloy 13-8 Stainless Steel in the annealed condition can be strengthened further by relatively low temperature heat treatment.
PRODUCT PROFILE & DIMENSIONS
Round bar / Disc (diameter): 5.50mm to 600mm
Square bar / Flat bar: 10mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T6 - 200mm X W1000- 2500mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W600- 1000mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Other different shapes based on OEM
ADVANTAGE & SUPERIOR SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
CNC saw cutting.
Marking by stamping or printing.
Third party inspection service.
Export packing / Export documents.
Transport by Track, Sea, Courier (FedEx, UPS, DHL) and Air Cargo.
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
CNC saw cutting.
Marking by stamping or printing.
Third party inspection service.
Export packing / Export documents.
Transport by Track, Sea, Courier (FedEx, UPS, DHL) and Air Cargo.
Hot search：1.4534 / X3CrNiMoAl13-8-2
Previous page：Z3NCUD28-20
Last page：Grade 704A60
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1