Round bar, Flat bar, X13CrMnMoN18-14-3 Austenitic Stainless Steel, ESR melting, Hot forging / rolling, Heat treatment, Hot working
TECHNICAL DATA SHEET - X13CrMnMoN18-14-3
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Austenitic type stainless steel
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (％): ≤ 0.15
Silicon, Si (％): ≤ 1.00
MATERIAL CATEGORY: Austenitic type stainless steel
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (％): ≤ 0.15
Silicon, Si (％): ≤ 1.00
Manganese, Mn (％): 12.0 ~ 16.0
Phosphorus, P (％) ≤: 0.050
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 16.0 ~ 20.0
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 16.0 ~ 20.0
Nickel, Ni (%): ≤ 0.30
Molybdenum, Mo (％): 2.50 ~ 4.20
Aluminum, Al (%): ≤ 0.10
Niobium, Nb (%): ≤ 0.25
Vanadium, V (%): ≤ 0.20
Nitrogen, N (%): 0.50 ~ 1.00
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: annealing 1050 ~ 1100 Deg. water cooled
Tensile strength, Rm ≥ MPa: 810 max.
Yield strength, Rp0.2 ≥ MPa: 450
Elongation, EL, A5 ≥ (％): 20.0
Yield strength, Rp0.2 ≥ MPa: 450
Elongation, EL, A5 ≥ (％): 20.0
Reduction of area, Z (%): -
Annealed hardness, HB ≤: 289
PRODUCT DESCRIPTION
The alloy is usually produced by IFF + AOD + VD, AOD + EF / EAF + VD, followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution annealed.
The alloy is usually produced by IFF + AOD + VD, AOD + EF / EAF + VD, followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution annealed.
PRODUCT PROFILE AND DIMENSIONS
Round bar / rod / disc (diameter): 5.50 ~ 650mm
Square bar / Flat bar: T10 ~ 500 X W15 ~ 1000mm
Round bar / rod / disc (diameter): 5.50 ~ 650mm
Square bar / Flat bar: T10 ~ 500 X W15 ~ 1000mm
Wire rod (diameter): 3.0 ~ 14mm
Strip: T0.50 ~ 3.0 X W 8.0 ~ 650mm
Other sizes can be supplied to meet specific requirements.
Other sizes can be supplied to meet specific requirements.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, please EMAIL (sales@ccsteels.com) our qualified production engineers.
If you meet further on any technical enquiry, please EMAIL (sales@ccsteels.com) our qualified production engineers.
Hot search：X13CrMnMoN18-14-3
Previous page：Z8CNUF18-09
Last page：Haynes 36
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1