1.4452
2018-07-02 11:41:51 Origin: Remark:0 Click:
Austenitic stainless steel 1.4452 Round bar, flat bar, Forgings 1.4452 ESR melting, Hot forging, Hot rolling, Heat treatment, Cold working or Machined.
TECHNICAL DATA SHEET - Grade DIN 1.4452
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Hot worked non-magnetic stainless steel
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): ≤ 0.15
Silicon, Si (%): ≤ 1.00
MATERIAL CATEGORY: Hot worked non-magnetic stainless steel
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): ≤ 0.15
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): 12.0 ~ 16.0
Phosphorus, P (%) ≤: 0.050
Sulfur, S (%) ≤: 0.030
Chromium, Cr (%): 16.0 ~ 20.0
Sulfur, S (%) ≤: 0.030
Chromium, Cr (%): 16.0 ~ 20.0
Nickel, Ni (%): ≤ 0.30
Molybdenum, Mo (%): 2.50 ~ 4.20
Aluminum, Al (%): ≤ 0.10
Niobium, Nb (%): ≤ 0.25
Vanadium, V (%): ≤ 0.20
Nitrogen, N (%): 0.50 ~ 1.00
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: annealing 1050 ~ 1100 Deg. water cooled
Tensile strength, TS, σb/≥ MPa: 810 max.
Yield strength, YS, σ0.2/≥ MPa: 450
Elongation, EL, δ ≥(%): 20.0
Yield strength, YS, σ0.2/≥ MPa: 450
Elongation, EL, δ ≥(%): 20.0
Reduction of area, RA, (%): -
Annealed hardness, HB ≤: 289
PRODUCT DESCRIPTION
The alloy is usually produced by IFF + AOD + VD, AOD + EF / EAF + VD, followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment or based on the buyer's special requirements.
The alloy is usually produced by IFF + AOD + VD, AOD + EF / EAF + VD, followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered thermal treatment or based on the buyer's special requirements.
PRODUCT PROFILE AND DIMENSIONS
Round bar (Diameter): 5.50mm to 650mm
Square bar / Flat bar: T3 to 500mm X W3 ~ 1200mm
Round bar (Diameter): 5.50mm to 650mm
Square bar / Flat bar: T3 to 500mm X W3 ~ 1200mm
Wire rod (Diameter): 0.50mm to 16mm
Strip: T0.20~3.0 X W8.0~650mm
Length: Fixed length or random length or based on the customer's special requirement.
Length: Fixed length or random length or based on the customer's special requirement.
Other sizes can be supplied to meet specific requirements.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, please EMAIL our qualified production engineers. - E-mail: sales@ccsteels.com.
If you meet further on any technical enquiry, please EMAIL our qualified production engineers. - E-mail: sales@ccsteels.com.
Hot search:1.4452
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1