Technical specifications of American high temperature alloys AMS 5796 Round bar, Flat bar, Forgigns, L605 Alloy steel ESR & VAR technique, Hot forging /rolling, Heat treatment
TECHNICAL DATA SHEET - AMS 5796 & Alloy L605
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Cr - Ni - W - Co base alloy
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.05 ~ 0.15
Silicon, Si (％): ≤ 0.40
Manganese, Mn (％): 1.00 ~ 2.00
Phosphorus, P (％)≤: 0.025
Carbon, C (％): 0.05 ~ 0.15
Silicon, Si (％): ≤ 0.40
Manganese, Mn (％): 1.00 ~ 2.00
Phosphorus, P (％)≤: 0.025
Sulfur, S (％)≤: 0.015
Chromium, Cr (％): 19.0 ~ 21.0
Chromium, Cr (％): 19.0 ~ 21.0
Nickel, Ni (％): 9.00 ~ 10.0
Molybdenum, Mo (％): -
Cobalt, Co (%): Remainder
Cobalt, Co (%): Remainder
Tungsten, W (%): 14.0 ~ 16.0
Aluminum, Al (%): -
Aluminum, Al (%): -
Copper, Cu (%): -
Titanium, Ti (%): -
Titanium, Ti (%): -
Ferrum, Fe (% ): ≤ 3.0
MECHANICAL PROPERTIES
Tensile strength, σb ≥ MPa: 1005
Yield strength, σ0.2 MPa: 480
Elongation, δ ≥ (％): 51.0
Reduction of area, ф ≥ (％): -
Hardness via heat treatment /HBW: HRC33 ~ 43
Reduction of area, ф ≥ (％): -
Hardness via heat treatment /HBW: HRC33 ~ 43
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged or Double aged.
FORMS AND DIMENSIONS
Round bar (Diameter): 5.50 ~ 450mm
Square bar / Flat bar: 10 ~ 350mm
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged or Double aged.
FORMS AND DIMENSIONS
Round bar (Diameter): 5.50 ~ 450mm
Square bar / Flat bar: 10 ~ 350mm
Wire rod (diameter): 0.10 ~ 16mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Other sizes can be supplied to meet specific requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our qualified production engineers.
If you meet further on any technical enquiry, pleased to EMAIL our qualified production engineers.
E-mail: sales@ccsteels.com.
Previous page：Haynes HR160
Last page：N12160
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1