S42400 is a 13% Chromium - 4.0% Nickel Martenstic Steel, Forging, Round bar, Flat bar, S42400 stock Equivalent Steel, Heat treatment
MATERIAL DATA SHEET - S42400
MATERIAL CATEGORY - 13Cr-4Ni-Mo martensitic type
PRODUCT DESCRIPTION
S42400 is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - QT + SRA.
S42400 is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - QT + SRA.
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580
PRODUCT PROFILE & DIMENSIONS
Round bar / disc / rod (diameter): 5.5 ~ 800mm
Square bar / Flat bar: 8 ~ 600mm
Plate / Sheet steel / Steel strip: 0.1mm to 200mm
Width: 8mm to 1500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
Round bar / disc / rod (diameter): 5.5 ~ 800mm
Square bar / Flat bar: 8 ~ 600mm
Plate / Sheet steel / Steel strip: 0.1mm to 200mm
Width: 8mm to 1500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (%): ≤ 0.06
Silicon, Si (%): 0.30 ~ 0.60
Manganese, Mn (%): 0.50 ~ 1.00
Phosphorus, P (%) ≤: 0.030
Sulfur, S (%) ≤: 0.020
Chromium, Cr (%): 12.0 ~ 14.0
Nickel, Ni (%): 3.50 ~ 4.50
Molybdenum, Mo (%): 0.30 ~ 0.70
Silicon, Si (%): 0.30 ~ 0.60
Manganese, Mn (%): 0.50 ~ 1.00
Phosphorus, P (%) ≤: 0.030
Sulfur, S (%) ≤: 0.020
Chromium, Cr (%): 12.0 ~ 14.0
Nickel, Ni (%): 3.50 ~ 4.50
Molybdenum, Mo (%): 0.30 ~ 0.70
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Form: heavy plate, sheet, strip
Tensile strength, Rm / MPa: 550
Yield strength, Rp0.2 / MPa: 360
Elongation, A5 (%): 16
Reduction of area, Z (%): -
Elongation, A5 (%): 16
Reduction of area, Z (%): -
Hardness (HBW): -
Hardness | HRB: 88
Cold bending property: -
TYPICAL APPLICATIONS
Chemical equipment, Bolt and nuts, Pressure vessel.
Mechanical parts used in the condition of corrosion resistance.
Chemical equipment, Bolt and nuts, Pressure vessel.
Mechanical parts used in the condition of corrosion resistance.
TECHNICAL SALES ASSISTANCE & SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
CNC saw cutting.
Marking by stamping or printing.
Third party inspection service.
Export packing / Export documents.
Transport by Track, Sea, Courier (FedEx, UPS, DHL) and Air Cargo.
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email:sales@ccsteels.com.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
CNC saw cutting.
Marking by stamping or printing.
Third party inspection service.
Export packing / Export documents.
Transport by Track, Sea, Courier (FedEx, UPS, DHL) and Air Cargo.
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email:sales@ccsteels.com.
Hot search:S42400
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1