XM-8
2014-10-08 15:49:49 Origin： Remark：0 Click：
XM-8 a 18% Chromium - 0.60% Titanium ferrite stainless steel, Round bar, S43035 Flat bar, plate AISI 439 Specifications Steel melting, ESR melted, Hot forging / Hot rolling, Heat treatment, Ultrasonic test, Cold worked.
MATERIAL TECHNICAL DATASHEET - AISI 439 / ASTM XM-8 / UNS S43035
MATERIAL CATEGORY: 18Cr-Ti Ferrite type
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580
The alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580
CHEMICAL COMPOSITION (mass weight %)
C (％): ≤ 0.030
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 17.0 ~ 19.0
Ni (％): ≤ 0.50
Mo (％): -
Other(％): 0.20+4(C+N) ≤ Ti ≤ 1.10, Al≤0.15, N ≤0.030
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 17.0 ~ 19.0
Ni (％): ≤ 0.50
Mo (％): -
Other(％): 0.20+4(C+N) ≤ Ti ≤ 1.10, Al≤0.15, N ≤0.030
MECHANICAL PROPERTIES FINAL HEAT TREATMENT
Form: heavy plate, sheet, strip
Tensile strength, σb/MPa: 415
Yield strength, σ0.2/MPa: 205
Elongation, δ (％): 22
Reduction of area, ф (％): -
Elongation, δ (％): 22
Reduction of area, ф (％): -
Hardness (HBW): 183
Hardness | HRB: 89
Cold bending property: 180D
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
TYPICAL APPLICATIONS
Chemical equipment and parts.
Mechanical parts used in the condition of corrosion resistance
Bolt and nuts, Pressure vessel.
Mechanical parts used in the condition of corrosion resistance
Bolt and nuts, Pressure vessel.
PRODUCT PROFILE & DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 500mm
Square bar / Flat bar: 3mm to 600mm
Plate / Sheet steel / Steel strip: 10mm to 1200mm
Width: 8mm to 1500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
Square bar / Flat bar: 3mm to 600mm
Plate / Sheet steel / Steel strip: 10mm to 1200mm
Width: 8mm to 1500mm
Length: random length or based on the customer's special requirement.
Forged steel shape: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Hot search：XM-8
Previous page：AISI 439
Last page：UNS S43035
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1