403Cb+ / 1.4913 Stockist, 403Cb+ / 1.4913 Equivalent Steel

403Cb+ / 1.4913
2024-12-05 15:31:00   Origin:   Remark:0 Click:

Martensitic Steel 403Cb Round bar, Flat bar, Forgings S41041 Stock Available, ESR 1.4913 Blade Steel, Hot forging / rolling, Heat treatment
 
TECHNICAL DATA SHEET - 1.4913 & AISI 403Cb+

OFFICIAL TEST CERTIFICATE - issued by TUV - SGSBV
MATERIAL CATEGORY - High temperature martensitic high content chromium alloy steel
MATERIAL SPECIFICATIONS - ASTM A565
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (%): 0.13 ~ 0.18
Silicon, Si (%): ≤ 0.50
Manganese, Mn (%): 0.40 ~ 0.60
Phosphorus, P (%) ≤: 0.030
Sulfur, S (%) ≤: 0.030
Chromium, Cr (%): 11.5 ~ 13.0
Nickel, Ni (%): ≤ 0.50
Molybdenum, Mo (%): ≤ 0.20
Niobium, Nb (%): 0.15 ~ 0.45
Other (%): Al ≤ 0.05
MECHANICAL PROPERTIES UNDER ROOM TEMP.  
Condition of heat treatment: HT 1136 ~ 1163 ℃, ≥ 677℃ X 2h tempered
Tensile strength, σb ≥ MPa: 795
Yield strength, σ0.2 ≥ MPa: 515
Elontation, δ5 ≥ (%): 15.0
Reduction of area, Z ≥ (%): 50.0
Hardness | HRS:  ≤ 277
PRODUCT DESCRIPTION
The
alloy is usually produced by AOD / VOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - Quenched and tempered + SRA.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL our resident team of qualified production engineers. - Email:
lh.steel@hotmail.com  

Hot search:403Cb

Previous page:ASTM A565 Gr.619
Last page:21CrMoV5-7

Share to: