X17CrMoVNbB9-1
2024-11-20 04:44:00 Origin： Remark：0 Click：
EN 10027 Specifications X17CrMoVNbB9-1 Round bar, Flat bar, Forgings, X17CrMoVNbB9-1 Stock Available, ESR melting, Heat treatment, Cold working
TECHNICAL DATA SHEET - X17CrMoVNbB9-1
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY - High temperature alloy steel
MATERIAL SPECIFICATIONS: DIN EN 10027
CHEMICAL COMPOSITIONS (mass weight - %)
Carbon, C (％): 0.12~ 0.19
Silicon, Si (％): ≤ 0.10
Manganese, Mn (％): ≤ 0.15
Silicon, Si (％): ≤ 0.10
Manganese, Mn (％): ≤ 0.15
Phosphorus, P (％) ≤: 0.020
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): 8.50 ~ 9.50
Nickel, Ni (％): ≤ 0.30
Sulfur, S (％) ≤: 0.010
Chromium, Cr (％): 8.50 ~ 9.50
Nickel, Ni (％): ≤ 0.30
Molybdenum, Mo (%): 1.40 ~ 1.70
Vanadium, V (%): 0.24 ~ 0.30
Niobium, Nb (%): 0.04 ~ 0.07
Boron, B (%): 0.007 ~ 0.010
Other (％): Cu ≤ 0.15, N ≤ 0.020
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition of heat treatment: Quenching 1100 ~ 1120 Deg. 30 mins, min, Oil or air cooled
1st tempering 580~600 Deg, 3h min., air cooled
2nd tempering 690~730 Deg, 3h min, air cooled
Stress relieving, 650 ~ 730 Deg, 2h min
Tensile strength, σb ≥ MPa: 850 ~ 1000
Yield strength, σ0.2 ≥ MPa: 700
Yield strength, σ0.2 ≥ MPa: 700
Elontation, δ5 ≥ (％): 12.0
Reduction of area, ф ≥ (％): 40.0
Hardness | HBW: 255 ~ 302
Reduction of area, ф ≥ (％): 40.0
Hardness | HBW: 255 ~ 302
PRODUCT DESCRIPTION
The alloy is usually produced by BEF & AOD & VIM followed by electroslag remelting (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed or Q+T condition.
The alloy is usually produced by BEF & AOD & VIM followed by electroslag remelting (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed or Q+T condition.
FORMS AND DIMENSIONS
Round bar & rod & disc (diameter): 5.50 ~ 850mm
Square bar / Flat bar: 8 ~ 400 mm
Forging piece: Different shapes based on OEM.
Round bar & rod & disc (diameter): 5.50 ~ 850mm
Square bar / Flat bar: 8 ~ 400 mm
Forging piece: Different shapes based on OEM.
Hot search：X17CrMoVNbB9-1
Total list
Monthly rank
- 29X35CrMo17
- 29ASTM A565 Gr.616HT
- 26Z15CN17-03
- 21X10CrNiW17-13-3
- 21ASTM A638 Gr.660
- 19AISI 306
- 17SAE 51420
- 16P550
- 15SAE 51416
- 14SAE 30304