X11CrNiWTi17-13-3
2019-05-17 15:41:25 Origin： Remark：0 Click：
Material technical specifications of High temperature alloy steels for internal combustion engine X11CrNiWTi17-13-3 datasheet, X11CrNiWTi17-13-3 Chemical compositions, X11CrNiWTi17-13-3 mechanical properties from Steelmaking, ESR melting, Hot blooming, UT, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or Machined. Technical specifications - ISO / TR 4956 - 1984, 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - X11CrNiWTi17-13-3
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: High temperature alloy steel for internal combustion engine
MATERIAL SPECIFICATIONS: ISO / TR 4956 - 1984
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.07 ~ 0.15
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.030
S (％)≤: 0.025
Cr (％): 15.5 ~ 17.5
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.030
S (％)≤: 0.025
Cr (％): 15.5 ~ 17.5
Ni (%): 12.0 ~ 14.5
Mo (％): -
Mo (％): -
W (%): 2.50 ~ 3.50
Ti (%): 4 X C ~ 0.80
B (%): ≤ 0.006
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition of heat treatment: Quenched and tempered
Tensile strength, σb ≥/MPa: 600 ~ 800
Yield strength, σ0.2 ≥/MPa: 430
Yield strength, σ0.2 ≥/MPa: 430
Elontation, δ ≥(％): 25.0
Reduction of area, ф ≥(％): -
Hardness | HBW: 240 max.
Reduction of area, ф ≥(％): -
Hardness | HBW: 240 max.
PRODUCT DESCRIPTION
The alloy is usually produced by BEF & AOD followed by electroslag remelting (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
The alloy is usually produced by BEF & AOD followed by electroslag remelting (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
FORMS AND SHAPES
Round bar (Diameter): 5.50 ~ 650mm
Square bar / Flat bar: 3 ~ 650mm
Round bar (Diameter): 5.50 ~ 650mm
Square bar / Flat bar: 3 ~ 650mm
Wire rod (Diameter): 0.10 ~ 16mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Hot search：X11CrNiWTi17-13-3
Previous page：X5CND16.5
Last page：X11CrNiWTi17-13-3
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1