N06625 & Alloy 625 is a 21% Chromium - 62% Nickel Base Alloy Steel, N06625 Round bar, flat bar, Sheet, and plate Steelmaking, ESR & VAR technique, Hot forging/rolling
TECHNICAL DATA SHEET - N06625 & Alloy 625
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Nickel base alloy
CHEMICAL COMPOSITION (mass weight %)
Carbon, C (％): ≤ 0.10
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): ≤ 0.50
Phosphorus, P (％) ≤: 0.015
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 20.0 ~ 23.0
Nickel, Ni (％): ≥ 58.0
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): ≤ 0.50
Phosphorus, P (％) ≤: 0.015
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 20.0 ~ 23.0
Nickel, Ni (％): ≥ 58.0
Copper, Cu (％): -
Aluminium, Al (%): ≤ 0.40
Titanium, Ti (%): ≤ 0.40
Ferrum, Fe (%): ≤ 5.00
Molybdenum, Mo (%): 8.00 ~ 10.0
Niobium, Nb + Ta (%): 3.15 ~ 4.15
TYPICAL MECHANICAL PROPERTIES
Solution treated: ≥ 1090, rapid cooled
Annealed: ≥ 870, rapid cooled
Ageing treated: -
Condition: A
Tensile strength, σb/≥ MPa: 830
Yield strength, σ0.2/≥ MPa: 415
Elongation, δ ≥(％): 30
Hardness | HBW ≤: -
Yield strength, σ0.2/≥ MPa: 415
Elongation, δ ≥(％): 30
Hardness | HBW ≤: -
Suitable size /mm: 100
Tensile strength, σb/≥ MPa: 760
Yield strength, σ0.2/≥ MPa: 380
Elongation, δ ≥(％): 30
Hardness | HBW ≤: -
Yield strength, σ0.2/≥ MPa: 380
Elongation, δ ≥(％): 30
Hardness | HBW ≤: -
Suitable size /mm: 100 ~ 250
Condition: S
Tensile strength, σb/≥ MPa: 690
Yield strength, σ0.2/≥ MPa: 275
Elongation, δ ≥(％): 30
Hardness | HBW ≤: -
Yield strength, σ0.2/≥ MPa: 275
Elongation, δ ≥(％): 30
Hardness | HBW ≤: -
TYPICAL APPLICATIONS
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged or Double aged.
AVAILABLE FORMS AND DIMENSIONS
Round bar (Diameter): 5.5 ~ 450mm
Square bar / Flat bar: 3 ~ 350mm
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged or Double aged.
AVAILABLE FORMS AND DIMENSIONS
Round bar (Diameter): 5.5 ~ 450mm
Square bar / Flat bar: 3 ~ 350mm
Wire rod (Diameter): 0.10 ~ 16mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 350mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 350mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Other sizes can be supplied to meet specific requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our qualified production engineers,
If you meet further on any technical enquiry, pleased to EMAIL our qualified production engineers,
Email us: sales@ccsteels.com.
Previous page：Inconel 625
Last page：Inconel 625LCF / Alloy 626
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1