Material technical specification of KS D3706 stainless steel round bar STS316L datasheet,STS316L Chemical compositions, Grade STS316L Mechanical properties from Remelting, ESR refining, Hot blooming, Billet UT, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or Machined. Technical specifications - KS D3706 - 2001/2006.
TECHNICAL DATA SHEET - KS D3706 Grade STS316L
TECHNICAL SPECIFICATIONS: KS D3706 - 2001 / 2006
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Austenitic Stainless steel rod
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.030
Si (％): ≤ 1.50
Mn (％): ≤ 2.00
P (％) ≤: 0.045
S (％) ≤: 0.030
Cr (％): 16.0 ~ 18.0
Ni (％): 12.0 ~ 15.0
Mo (%): 2.00 ~ 3.00
N (%): -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/ ≥ MPa: 480
Yield strength, σ0.2/ ≥ MPa: 175
Elongation, δ (％) ≥: 40.0
Reduction of area, ф (％) ≥: 60.0
Hardness ≤ (HBW): 187
HEAT TREATMENT PRACTICE
Condition: solution annealed 1030 ~ 1150 Deg.C
Cooling medium: Rapid cool
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT DESCRIPTION
Round bar (Diameter): 5.50 ~ 550mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (width X thickness): 1 ~ 400 X 4 ~ 1000mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to EMAIL ( lh.steel@hotmail.com ) our resident team of qualified production engineers.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Austenitic Stainless steel rod
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.030
Si (％): ≤ 1.50
Mn (％): ≤ 2.00
P (％) ≤: 0.045
S (％) ≤: 0.030
Cr (％): 16.0 ~ 18.0
Ni (％): 12.0 ~ 15.0
Mo (%): 2.00 ~ 3.00
N (%): -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/ ≥ MPa: 480
Yield strength, σ0.2/ ≥ MPa: 175
Elongation, δ (％) ≥: 40.0
Reduction of area, ф (％) ≥: 60.0
Hardness ≤ (HBW): 187
HEAT TREATMENT PRACTICE
Condition: solution annealed 1030 ~ 1150 Deg.C
Cooling medium: Rapid cool
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT DESCRIPTION
Round bar (Diameter): 5.50 ~ 550mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (width X thickness): 1 ~ 400 X 4 ~ 1000mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to EMAIL ( lh.steel@hotmail.com ) our resident team of qualified production engineers.
Hot search：STS316L
Previous page：K33100
Last page：Grade F91 type 1
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1