Material technical specifications of KS D3706 stainless steel round bar STS316N datasheet, alloy STS316N Chemical compositions, STS316N Mechanical properties from Remelting, ESR refining, Hot blooming, Billet UT, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold working or Machined. Technical specifications - KS D3706 - 2001/2006.
TECHNICAL DATA SHEET - KS D3706 Grade STS316N
TECHNICAL SPECIFICATIONS: KS D3706 - 2001 / 2006
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Austenitic Stainless steel rod
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.08
Si (％): ≤ 1.50
Mn (％): ≤ 2.00
P (％) ≤: 0.045
S (％) ≤: 0.030
Cr (％): 16.0 ~ 18.0
Ni (％): 10.0 ~ 14.0
Mo (%): 2.00 ~ 3.00
N (%): 0.10 ~ 0.22
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/ ≥ MPa: 550
Yield strength, σ0.2/ ≥ MPa: 275
Elongation, δ (％) ≥: 35.0
Reduction of area, ф (％) ≥: 50.0
Hardness ≤ (HBW): 217
HEAT TREATMENT PRACTICE
Condition: solution annealed 1030 ~ 1150 Deg.C
Cooling medium: Rapid cool
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT DESCRIPTION
Round bar (Diameter): 5.50 ~ 550mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (width X thickness): 1 ~ 400 X 4 ~ 1000mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to EMAIL ( lh.steel@hotmail.com ) our resident team of qualified production engineers.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Austenitic Stainless steel rod
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.08
Si (％): ≤ 1.50
Mn (％): ≤ 2.00
P (％) ≤: 0.045
S (％) ≤: 0.030
Cr (％): 16.0 ~ 18.0
Ni (％): 10.0 ~ 14.0
Mo (%): 2.00 ~ 3.00
N (%): 0.10 ~ 0.22
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/ ≥ MPa: 550
Yield strength, σ0.2/ ≥ MPa: 275
Elongation, δ (％) ≥: 35.0
Reduction of area, ф (％) ≥: 50.0
Hardness ≤ (HBW): 217
HEAT TREATMENT PRACTICE
Condition: solution annealed 1030 ~ 1150 Deg.C
Cooling medium: Rapid cool
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT DESCRIPTION
Round bar (Diameter): 5.50 ~ 550mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (width X thickness): 1 ~ 400 X 4 ~ 1000mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to EMAIL ( lh.steel@hotmail.com ) our resident team of qualified production engineers.
Hot search：STS316N
Previous page：Grade F91 type 1
Last page：STS316LN
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1