STS836L
2019-10-16 08:53:43 Origin： Remark：0 Click：
Specification D3706 STS836L Datasheet, Suppliers STS836L Chemical, Inventory STS836L Stock properties from Remelting, ESR refining, Hot blooming, Billet UT, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic test, Cold working or Machined. Technical specifications - KS D3706 - 2001 / 2006.
TECHNICAL DATA SHEET - KS D3706 Grade STS836L
TECHNICAL SPECIFICATIONS - KS D3706 - 2001 / 2006
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
MATERIAL CATEGORY - Austenitic Stainless steel rod
CHEMICAL COMPOSITION ( Msss Weight % )
C (％): ≤ 0.030
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％) ≤: 0.035
S (％) ≤: 0.020
Cr (％): 19.0 ~ 24.0
Ni (％): 24.0 ~ 26.0
Mo (%): 5.00 ~ 7.00
N (%): ≤ 0.25
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/ ≥ MPa: 520
Yield strength, σ0.2/ ≥ MPa: 205
Elongation, δ (％) ≥: 35.0
Reduction of area, ф (％) ≥: 40.0
Hardness ≤ (HBW): 217
HEAT TREATMENT PRACTICE
Condition: solution annealed 1020 ~ 1060 Deg.C
Cooling medium: Rapid cool
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PROFILE & DIMENSIONS
Round bar (Diameter): 5.5 ~ 550mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (width X thickness): 1 ~ 400 X 4 ~ 700mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
OFFICIAL TEST CERTIFICATE - issued by TUV - SGS - BV
MATERIAL CATEGORY - Austenitic Stainless steel rod
CHEMICAL COMPOSITION ( Msss Weight % )
C (％): ≤ 0.030
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％) ≤: 0.035
S (％) ≤: 0.020
Cr (％): 19.0 ~ 24.0
Ni (％): 24.0 ~ 26.0
Mo (%): 5.00 ~ 7.00
N (%): ≤ 0.25
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/ ≥ MPa: 520
Yield strength, σ0.2/ ≥ MPa: 205
Elongation, δ (％) ≥: 35.0
Reduction of area, ф (％) ≥: 40.0
Hardness ≤ (HBW): 217
HEAT TREATMENT PRACTICE
Condition: solution annealed 1020 ~ 1060 Deg.C
Cooling medium: Rapid cool
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PROFILE & DIMENSIONS
Round bar (Diameter): 5.5 ~ 550mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (width X thickness): 1 ~ 400 X 4 ~ 700mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com.
Hot search：STS836L
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1