Technical specifications of KS D3706 stainless steel round bar STS 329J3L data sheet, STS329J3L Chemical compositions, STS329J3L Mechanical properties from Remelting, ESR refining,STS329J3L Hot blooming, Billet UT, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold worked or Machined. Technical specifications - KS D3706 - 2001 / 2006.
TECHNICAL DATA SHEET - KS D3706 Grade STS329J3L
TECHNICAL SPECIFICATIONS: KS D3706 - 2001 / 2006
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Austenite - ferrite Stainless steel rod
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.030
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％) ≤: 0.035
S (％) ≤: 0.020
Cr (％): 21.0 ~ 24.0
Ni (％): 4.50 ~ 6.50
Mo (%): 2.50 ~ 3.50
N (%): 0.08 ~ 0.20
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/ ≥ MPa: 620
Yield strength, σ0.2/ ≥ MPa: 450
Elongation, δ (％) ≥: 18.0
Reduction of area, ф (％) ≥: 40.0
Hardness ≤ (HBW): 302 max.
HEAT TREATMENT PRACTICE
Condition: solution annealed 950 ~ 1100 Deg.C
Cooling medium: Rapid cool
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT DESCRIPTION
Round bar (Diameter): 5.50 ~ 550mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (width X thickness): 1 ~ 400 X 4 ~ 900mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to EMAIL ( lh.steel@hotmail.com ) our resident team of qualified production engineers.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Austenite - ferrite Stainless steel rod
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.030
Si (％): ≤ 1.00
Mn (％): ≤ 2.00
P (％) ≤: 0.035
S (％) ≤: 0.020
Cr (％): 21.0 ~ 24.0
Ni (％): 4.50 ~ 6.50
Mo (%): 2.50 ~ 3.50
N (%): 0.08 ~ 0.20
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/ ≥ MPa: 620
Yield strength, σ0.2/ ≥ MPa: 450
Elongation, δ (％) ≥: 18.0
Reduction of area, ф (％) ≥: 40.0
Hardness ≤ (HBW): 302 max.
HEAT TREATMENT PRACTICE
Condition: solution annealed 950 ~ 1100 Deg.C
Cooling medium: Rapid cool
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT DESCRIPTION
Round bar (Diameter): 5.50 ~ 550mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (width X thickness): 1 ~ 400 X 4 ~ 900mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to EMAIL ( lh.steel@hotmail.com ) our resident team of qualified production engineers.
Hot search：STS329J3L
Previous page：STS329J4L
Last page：ASTM A182 type F911
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1