Material technical specifications of KS D3706 stainless steel Round bar STS405 Heat treatment, 100% Ultrasonic test, Cold worked or Machined.
TECHNICAL DATA SHEET - KS D3706 Grade STS405
TECHNICAL SPECIFICATIONS: KS D3706 - 2001 / 2006
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Ferrite series Stainless steel rod
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): ≤ 0.08
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): ≤ 1.00
Phosphorus, P (%) ≤: 0.035
Sulfur, S (%) ≤: 0.020
Chromium, Cr (%): 11.5 ~ 14.5
Nickel, Ni (%): ≤ 0.60
Molybdenum, Mo (%): -
Nitrogen, N (%): -
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Ferrite series Stainless steel rod
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%): ≤ 0.08
Silicon, Si (%): ≤ 1.00
Manganese, Mn (%): ≤ 1.00
Phosphorus, P (%) ≤: 0.035
Sulfur, S (%) ≤: 0.020
Chromium, Cr (%): 11.5 ~ 14.5
Nickel, Ni (%): ≤ 0.60
Molybdenum, Mo (%): -
Nitrogen, N (%): -
Aluminum, Al (%): 0.10 ~ 0.30
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/ ≥ MPa: 410
Yield strength, σ0.2/ ≥ MPa: 175
Elongation, δ (%) ≥: 20.0
Reduction of area, ф (%) ≥: 60.0
Hardness ≤ (HBW): 183 max.
HEAT TREATMENT PRACTICE
Condition: annealed 780 ~ 830 Deg.C
Cooling medium: air cool or slow cool
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT DESCRIPTION
Round bar (Diameter): 5.50 ~ 550mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (width X thickness): 1 ~ 400 X 4 ~ 1000mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to EMAIL (sales@ccsteels.com ) our resident team of qualified production engineers.
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/ ≥ MPa: 410
Yield strength, σ0.2/ ≥ MPa: 175
Elongation, δ (%) ≥: 20.0
Reduction of area, ф (%) ≥: 60.0
Hardness ≤ (HBW): 183 max.
HEAT TREATMENT PRACTICE
Condition: annealed 780 ~ 830 Deg.C
Cooling medium: air cool or slow cool
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT DESCRIPTION
Round bar (Diameter): 5.50 ~ 550mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (width X thickness): 1 ~ 400 X 4 ~ 1000mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to EMAIL (sales@ccsteels.com ) our resident team of qualified production engineers.
Hot search:STS405
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1