STS430F
2019-11-01 14:20:25 Origin: Remark:0 Click:
Material technical specification of KS D3706 stainless steel round bar STS430F datasheet,STS430F Chemical composition,STS430F Mechanical properties from Remelting, ESR refining, Hot blooming, Billet UT, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold worked or Machined. Technical specifications - KS D3706 - 2001 / 2006.
TECHNICAL DATA SHEET - KS D3706 Grade STS430F
TECHNICAL SPECIFICATIONS: KS D3706 - 2001 / 2006
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Ferrite series Stainless steel rod
CHEMICAL COMPOSITION (WEIGHT %)
C (%): ≤ 0.12
Si (%): ≤ 1.00
Mn (%): ≤ 1.50
P (%) ≤: 0.035
S (%) ≤: 0.15 Min.
Cr (%): 16.0 ~ 18.0
Ni (%): ≤ 0.60
Mo (%): -
N (%): -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/ ≥ MPa: 450
Yield strength, σ0.2/ ≥ MPa: 205
Elongation, δ (%) ≥: 22.0
Reduction of area, ф (%) ≥: 50.0
Hardness ≤ (HBW): 183 max.
HEAT TREATMENT PRACTICE
Condition: annealed 680 ~ 820 Deg.C
Cooling medium: air cool or slow cool
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT DESCRIPTION
Round bar (Diameter): 5.50 ~ 550mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (width X thickness): 1 ~ 400 X 4 ~ 1000mm
Length: random length, fixed length or based on the customer's special requirements.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to EMAIL ( lh.steel@hotmail.com ) our resident team of qualified production engineers.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Ferrite series Stainless steel rod
CHEMICAL COMPOSITION (WEIGHT %)
C (%): ≤ 0.12
Si (%): ≤ 1.00
Mn (%): ≤ 1.50
P (%) ≤: 0.035
S (%) ≤: 0.15 Min.
Cr (%): 16.0 ~ 18.0
Ni (%): ≤ 0.60
Mo (%): -
N (%): -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/ ≥ MPa: 450
Yield strength, σ0.2/ ≥ MPa: 205
Elongation, δ (%) ≥: 22.0
Reduction of area, ф (%) ≥: 50.0
Hardness ≤ (HBW): 183 max.
HEAT TREATMENT PRACTICE
Condition: annealed 680 ~ 820 Deg.C
Cooling medium: air cool or slow cool
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT DESCRIPTION
Round bar (Diameter): 5.50 ~ 550mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (width X thickness): 1 ~ 400 X 4 ~ 1000mm
Length: random length, fixed length or based on the customer's special requirements.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to EMAIL ( lh.steel@hotmail.com ) our resident team of qualified production engineers.
Hot search:STS430F
Previous page:K11597
Last page:A182 Grade F11 Class 2
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1