Austenitic Steel 2S131 Round bars, Flat bar, Plate S131 Forgings Steelmaking, Hot forging, Hot rolling, Heat treatment, Cold working or machined.

 

TECHNICAL DATA SHEET - 2S131
Material category - Aerospace "S" Series alloy steel
Stock Available - Round bar Diam. 12 ~ 60mm, ESR ingot.
Material sepcifications - BS EN 3890-2002, BS EN 2344-2001, BS EN 3146-2001
Melting process - Consumable electrode remelted
H S Code For Customs - 7228 4000 / 7228 5000 / 7228 6000
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (%):  0.55 ~ 0.70
Silicon, Si (%):  0.20 ~ 0.50
Manganese, Mn (%):  3.50 ~ 5.50
Phosphorus, P (%)≤:  0.035
Sulfur, S (%)≤:  0.025
Chromium, Cr (%):  3.00 ~ 4.00
Nickel, Ni (%):  11.0 ~ 14.0
Molybdenum, Mo (%):  ≤ 0.50
Nb/Ti (%):  -
Others (%): W ≤ 1.00, V ≤ 0.25
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: solution annealed
Tensile strength, Rm ≥ MPa: 620
Yield strength, Rp0.2 ≥ MPa: 300
Elongation, A5 ≥ (%): 35.0
Impact strength, AKU ≥ J: 300 min.
Hardness HBS:  -
Condition: work hardened
Tensile strength σb ≥ MPa: 950
Yield strength σs ≥ MPa: 740
Elongation δ5 ≥ (%): 30.0
Impact strength, AKV ≥ J:  -
Hardness HBS:  -
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / BEF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black condition.
Final heat treatment - solution treatment.
ADVANTAGE & SUPERIOR SERVICE
20+ years Focus On Special Steel Manufacturing and processing.
Stock over 60 grades with a competitive price, along with cutting service for specific requirement.
Customizing special material is welcome.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry or help, pleased to EMAIL our resident team of qualified production engineers, Email:sales@ccsteels.com