STS410J1 Stockist, STS410J1 Equivalent Steel

STS410J1
2019-11-18 09:36:57   Origin:   Remark:0 Click:

Material technical specification KS D3706 stainless steel round bar STS410J1 datasheet,STS410J1 Chemical compositions, STS410J1 Mechanical properties from Remelting,ESR,Hot blooming, Billet UT, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold worked or Machined. Technical specifications - KS D3706 - 2001 / 2006.
 
TECHNICAL DATA SHEET - KS D3706 Grade STS410J1

TECHNICAL SPECIFICATIONS: KS D3706 - 2001 / 2006
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS -  BV
MATERIAL CATEGORY: Martensite
 series Stainless steel rod
CHEMICAL COMPOSITION (WEIGHT %)
C (%):     0.08 ~ 0.18
Si (%):     ≤ 0.60
Mn (%):   ≤ 1.00
P (%) ≤:  0.030
S (%) ≤:  0.020
Cr (%):   11.5 ~ 14.0
Ni (%):    ≤ 0.60
Mo (%):   0.30 ~ 0.60
N (%):     -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/ ≥ MPa: 690
Yield strength, σ0.2/ ≥ MPa: 490
Elongation, δ (%) ≥: 20.0
Reduction of area, ф (%) ≥: 60.0
Hardness ≤ (HBW): 192 min.
HEAT TREATMENT PRACTICE
Condition: annealed 830 ~ 900 Deg.C
Cooling medium: slow cooling
Condition: quenched 970 ~ 1020 Deg.C, oil cooling, tempered 650 ~ 750 Deg.C, quick cooling
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT DESCRIPTION
Round bar (Diameter): 5.50 ~ 650mm
Wire rod (Diameter): 0.50 ~ 13mm
Flat bar (width X thickness): 10 ~ 400 X 10 ~ 900mm
Length: random length, fixed length or based on the customer's special requirements.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to
EMAIL ( lh.steel@hotmail.com ) our resident team of qualified production engineers.

Hot search:STS410J1

Previous page:STS410
Last page:K31545

Share to: