STS410F2 Stockist, STS410F2 Equivalent Steel

STS410F2
2019-11-27 11:24:48   Origin:   Remark:0 Click:

Material technical specifications of KS D3706 stainless steel round bar STS410F2 datasheet,alloy STS410F2 Chemical compositions, STS410F2 Mechanical properties from Remelting, ESR refining, Hot blooming, Billet UT, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic test, Cold worked or Machined. Technical specifications - KS D3706 - 2001 / 2006.
 
TECHNICAL DATA SHEET - KS D3706 Grade STS410F2

TECHNICAL SPECIFICATIONS: KS D3706 - 2001 / 2006
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS -  BV
MATERIAL CATEGORY: Martensite
 series Stainless steel rod
CHEMICAL COMPOSITION (WEIGHT %)
C (%):     ≤ 0.15
Si (%):     ≤ 1.00
Mn (%):   ≤ 1.00
P (%) ≤:  0.030
S (%) ≤:  0.020
Cr (%):   11.5 ~ 13.5
Ni (%):    ≤ 0.60
Mo (%):   -
N (%):     -
Pb (%):   0.05 ~ 0.30
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/ ≥ MPa: 540
Yield strength, σ0.2/ ≥ MPa: 345
Elongation, δ (%) ≥: 18.0
Reduction of area, ф (%) ≥: 50.0
Hardness ≤ (HBW): 159 min.
HEAT TREATMENT PRACTICE
Condition: annealed 800 ~ 900 Deg.C
Cooling medium: slow cooling
Condition: quenched 950 ~ 1000 Deg.C, oil cooling, tempered 700 ~ 750 Deg.C, quick cooling.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT DESCRIPTION
Round bar (Diameter): 5.50 ~ 550mm
Wire rod (Diameter): 2.50 ~ 13mm
Flat bar (width X thickness): 10 ~ 400 X 10 ~ 1000mm
Length: random length, fixed length or based on the customer's special requirements.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to
EMAIL ( lh.steel@hotmail.com ) our resident team of qualified production engineers.

Hot search:STS410F2

Previous page:A182 Grade F3VCb
Last page:K31390

Share to: