Alloy XM-16
2025-04-10 16:41:00 Origin： Remark：0 Click：
Specifications XM-16 Datasheet, Suppliers XM-16 Chemical, Inventory XM-16 Properties forgings From Melting, ESR & VAR technique, Hot forging / rolling
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
TECHNICAL DATA SHEET - AISI XM-16
MATERIAL CATEGORY - Precipitation hardening / heat resisting steel series
MATERIAL SPECIFICATIONS - ASTM A693 (2003)
CHEMICAL COMPOSITIONS (mass weight %)
Carbon, C (％): ≤ 0.05
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): ≤ 0.50
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 7.50 ~ 9.50
Molybdenum, Mo (％): ≤ 0.50
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): ≤ 0.50
Phosphorus, P (％) ≤: 0.040
Sulfur, S (％) ≤: 0.030
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 7.50 ~ 9.50
Molybdenum, Mo (％): ≤ 0.50
Copper, Cu (%): 1.50 ~ 2.50
Titanium, Ti (%): 0.80 ~ 1.40
Other (％): Nb+Ta 0.10 ~ 0.50
MECHANICAL PROPERTIES UNDER SOLUTION TREATMENT
Solution treatment temperature and cooling ways: 829 +/-15℃, water quenched
Steel plate thickness /mm: ≥ 0.25
Tensile strength, σb ≥ MPa: 1205
Yield strength, σ0.2 ≥ MPa: 1105
Elongation, δ5 ≥ (％): 3.0
Hardness ≤ HRC: 36
Hardness ≤ HBS: 361
Yield strength, σ0.2 ≥ MPa: 1105
Elongation, δ5 ≥ (％): 3.0
Hardness ≤ HRC: 36
Hardness ≤ HBS: 361
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - solution treatment / QT
The alloy is usually produced by AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright in the annealed condition.
Final heat treatment - solution treatment / QT
FORMS & DIMENSIONS
Rod / round bar / disc (diameter): 5.5mm to 550mm
Square bar / flat bar: 8mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Rod / round bar / disc (diameter): 5.5mm to 550mm
Square bar / flat bar: 8mm to 600mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 300mm X W50 - 1200mm X L1000-12000mm
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 300mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shaft, and other different shapes based on OEM.
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Sheet steel via cold rolled: T0.5 - 6mm X W10 - 300mm X L1000 - 2000mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: stepped shaft, and other different shapes based on OEM.
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Automobile parts, exhaust pipe
Electronics
Turbine motor blade
Bolts and nuts
Bolts and nuts
Forging valve
Pressure vessel
Pressure vessel
TECHNICAL SALES ASSISTANCE