AMS 5663 Round bar, Inconel 718 instock, AMS 5663 made from Vacuum Melting, ESR & VAR Remelt, technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test,
TECHNICAL DATA SHEET - AMS 5663
TECHNICAL SPECIFICATION: AMS 5663
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Precipitation hardened and cold worked nickel alloy
CHEMICAL COMPOSITION (mass weight %)
C (%): ≤ 0.08
Si (%): ≤ 0.35
Mn (%): ≤ 0.35
P (%) ≤: 0.015
S (%) ≤: 0.015
Cr (%): 17.0 ~ 21.0
Co (%): ≤ 1.00
Mo (%): 2.80 ~ 3.30
Nb/Ta (%): 4.75 ~ 5.50
Ti (%): 0.65 ~ 1.15
Al (%): 0.20 ~ 0.80
Zr (%): -
B (%): ≤ 0.006
Fe (%): Remainder
Cu (%): ≤ 0.30
Ni (%): 50.0 ~ 55.0
Ta (%): -
Ni (%): 50.0 ~ 55.0
Ta (%): -
Nb (%): -
W (%): -
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: Solution + Stabilize + Precipitation harden
W (%): -
MECHANICAL PROPERTIES UNDER ROOM TEMPERATURE
Condition: Solution + Stabilize + Precipitation harden
Heat treatment pratice: Solution treatment 924 ~ 1010 Deg. hold 1/2h min., cool at rate equivalent to air cool or faster
Precipitation hardening treatment, 718+/-14 Deg, hold at temperature for 8h, furnace cool to 621+/-14 Deg., hold until total precipitation heat treatment time has reached 18h, air cool
Tensile strength,σb/≥ MPa: 1275
Tensile strength,σb/≥ MPa: 1275
Yield strength, σ0.2/≥ MPa: 1034
Elongation, δ ≥(%): 12.0
Reduction of area, ф ≥ (%): 15.0
Hardness | HBW: 331 min.
STRESS RUPTURE REQUIREMENT
Test temperature: 649 Deg.
Stress /MPa: 690
Time to rupture: 23h
Elongtation, (%): 5.0
PRODUCT SHAPES & DIMENSIONS
Round bar (Diameter): 0.5mm to 550mm
Square bar / Flat bar: 10mm to 700mm
Forging piece: stepped shafts, and other different shapes based on OEM.
Elongation, δ ≥(%): 12.0
Reduction of area, ф ≥ (%): 15.0
Hardness | HBW: 331 min.
STRESS RUPTURE REQUIREMENT
Test temperature: 649 Deg.
Stress /MPa: 690
Time to rupture: 23h
Elongtation, (%): 5.0
PRODUCT SHAPES & DIMENSIONS
Round bar (Diameter): 0.5mm to 550mm
Square bar / Flat bar: 10mm to 700mm
Forging piece: stepped shafts, and other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1