STS630 H1025 Steel Ex-stock, Alloy STS630 H1025 Suppliers & Manufacturers,STS630 Forging Bar Plate machined, STS630 H1025 Blade Steel Exporters Technical specifications - KS D3706 - 2001 / 2006. From Melting, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic flaw detection test.
TECHNICAL DATA SHEET - KS D3706 Grade STS630
TECHNICAL SPECIFICATIONS: KS D3706 - 2001/2006
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Martensitic stainless steel rod
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.07
Si (％): ≤ 1.00
Mn (％): ≤ 1.50
P (％) ≤: 0.040
S (％) ≤: 0.030
Cr (％): 15.0 ~ 17.0
Ni (％): 3.00 ~ 5.00
Mo (%): -
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Martensitic stainless steel rod
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.07
Si (％): ≤ 1.00
Mn (％): ≤ 1.50
P (％) ≤: 0.040
S (％) ≤: 0.030
Cr (％): 15.0 ~ 17.0
Ni (％): 3.00 ~ 5.00
Mo (%): -
Cu (%): 3.00 ~ 5.00
Nb (%): 0.15 ~ 0.45
N (%): -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: Solution treated, 1020 ~ 1060 Deg.C
Tensile strength, σb/ ≥ MPa:-
Yield strength, σ0.2/ ≥ MPa: -
Elongation, δ (％) ≥: -
Reduction of area, ф (％) ≥: -
Hardness ≤ (HBW): 363
N (%): -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Condition: Solution treated, 1020 ~ 1060 Deg.C
Tensile strength, σb/ ≥ MPa:-
Yield strength, σ0.2/ ≥ MPa: -
Elongation, δ (％) ≥: -
Reduction of area, ф (％) ≥: -
Hardness ≤ (HBW): 363
Aged H1025, 540 ~ 560 Deg.C, air cooled
Tensile strength, σb/ ≥ MPa:1070
Yield strength, σ0.2/ ≥ MPa: 1000
Elongation, δ (％) ≥: 12.0
Reduction of area, ф (％) ≥: 45.0
Hardness ≤ (HBW): 331 min.
Tensile strength, σb/ ≥ MPa:1070
Yield strength, σ0.2/ ≥ MPa: 1000
Elongation, δ (％) ≥: 12.0
Reduction of area, ф (％) ≥: 45.0
Hardness ≤ (HBW): 331 min.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.50 ~ 600mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (width X thickness): 10 ~ 400 X 10 ~ 650mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.50 ~ 600mm
Wire rod (Diameter): 0.15 ~ 15mm
Flat bar (width X thickness): 10 ~ 400 X 10 ~ 650mm
Length: random length, fixed length or based on the customer's special requirement.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry. pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1