Description 1.3912 Plate Stocklist, Suppliers 1.3912 Round bar, Inventory 1.3912 Shaft Properties from Steelmaking, ESR melted, Hot rolling, Heat treatment
TECHNICAL DATA SHEET - 1.3912
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
CHEMICAL COMPOSITION (mass weight - %)
Carbno, C (%): ≤ 0.10
Silicon, Si (%): ≤ 0.35
Manganese, Mn (%): ≤ 0.60
Phosphorus, P (%) ≤: 0.025
Sulfur, S (%) ≤: 0.025
Chromium, Cr (%): ≤ 0.50
Nickel, Ni (%): 35.0 ~ 38.0
Molybdenum, Mo (%): ≤ 0.50
Silicon, Si (%): ≤ 0.35
Manganese, Mn (%): ≤ 0.60
Phosphorus, P (%) ≤: 0.025
Sulfur, S (%) ≤: 0.025
Chromium, Cr (%): ≤ 0.50
Nickel, Ni (%): 35.0 ~ 38.0
Molybdenum, Mo (%): ≤ 0.50
Cobalt, Co (%): ≤ 1.00
Ferrum, Fe (%): Remainder
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Tensile strength, Rm ≥ MPa: 490
Yield strength, Rp0.2 ≥ MPa: 310
Elongation, A5 ≥ (%): 30.0
Reduction of area, Z ≥ (%): -
Hardness via heat treatment /HBW: 140
Reduction of area, Z ≥ (%): -
Hardness via heat treatment /HBW: 140
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution treated + Aged
FORMS AND DIMENSIONS
Round bar (Diameter): 5.5mm to 450mm
Square bar / Flat bar: 3mm to 500mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Square bar / Flat bar: 3mm to 500mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 200mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry. pleased to Email our resident team of qualified production engineers. - Email: sales@ccsteels.com
If you meet further on any technical enquiry. pleased to Email our resident team of qualified production engineers. - Email: sales@ccsteels.com
Hot search:1.3912
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1