S44700
2014-10-09 15:18:46 Origin: Remark:0 Click:
UNS S44700 is defined as an ultralow carbon high 29.0 Chromium - 4.0 Molybdenum Ferrite Stainless steel available in form of round bar, flat bar, Steel strip. Material Standards ASTM A276 Steelmelting (ESR refined), Blooming, Hot forging, Hot rolling, Heat treated, Cold working or Machined.
MATERIAL DATA SHEET - Grade UNS S44700
MATERIAL CATEGORY - 29Cr-4Mo Ferrite type
MATERIAL SPECIFICATIONS - ASTM A959 (2004), A276, A312, A632, A176, A580
HS Code For customs - 72221100 / 72222000
CHEMICAL COMPOSITION ( Mass Weight % )
Carbon, C (%): ≤ 0.010
Silicon, Si (%): ≤ 0.20
Manganese, Mn (%): ≤ 0.30
Phosphorus, P (%)≤: 0.025
Sulfur, S (%)≤: 0.020
Chromium, Cr (%): 28.0 ~ 30.0
Nickel, Ni (%): ≤ 0.15
Molybdenum, Mo (%): 3.50 ~ 4.20
Copper, Cu (%): ≤ 0.15
Carbon, C (%): ≤ 0.010
Silicon, Si (%): ≤ 0.20
Manganese, Mn (%): ≤ 0.30
Phosphorus, P (%)≤: 0.025
Sulfur, S (%)≤: 0.020
Chromium, Cr (%): 28.0 ~ 30.0
Nickel, Ni (%): ≤ 0.15
Molybdenum, Mo (%): 3.50 ~ 4.20
Copper, Cu (%): ≤ 0.15
Nitrogen, N (%): ≤ 0.020
C+N (%): ≤ 0.025
MECHANICAL PROPERTIES UNDER HEAT TREATMENT
Form: Round bar, strip, hollow bar, flat bar
Heat treament practice: annealed 900 ~ 1050 Deg. quick cooling.
Tensile strength, σb/MPa: 550
Yield strength, σ0.2/MPa: 415
Elongation, δ(%): 20
Reduction of area, ф(%): -
Elongation, δ(%): 20
Reduction of area, ф(%): -
Hardness (HBW): 223
Hardness | HRB: (HRC20)
Cold bending property: 180 degree
HEAT TREATMENT PRACTICE
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult with the heat treatment provider for whole guidance on heat treatment of stainless steel grades. We are delighted to help to work with you the special heat treatment based on your special requirements.
PRODUCT DESCRIPTION
The alloy is usually produced by VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
TYPICAL APPLICATIONS
Chemical equipments, Mechanical parts used in the condition of corrosion resistance
Bolts and nuts, Pressure vessel, Medical components
The alloy is usually produced by VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
TYPICAL APPLICATIONS
Chemical equipments, Mechanical parts used in the condition of corrosion resistance
Bolts and nuts, Pressure vessel, Medical components
PROFILE & FORMS DIMENSIONS
Round bar / wire rod (Diameter): 5.5mm to 400mm
Square bar / flat bar: 3mm to 600mm
Plate / sheet steel / steel strip: 0.5mm to 600mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Other different shapes based on OEM.
Round bar / wire rod (Diameter): 5.5mm to 400mm
Square bar / flat bar: 3mm to 600mm
Plate / sheet steel / steel strip: 0.5mm to 600mm
Width: 8mm to 1000mm
Length: random length or based on the customer's special requirement.
Other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers, Email: sales@ccsteels.com
Hot search:S44700
Previous page:ASTM 29-4
Last page:ASTM 29-4C
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1