Stocklist AMS 5623 Round bar, Description AMS 5623 Shaft AMS 5623 forgings Properties from steelmaking, Electroslag remelting, blooming, Ultrasonic testing, hot forging, Hot rolling, Heat treatment, Cold working, Straightening.
TECHNICAL DATA SHEET - Grade AMS 5623
MATERIAL CATEGORY: Aerospace "S" Series alloy steel
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL SPECIFICATIONS: SAE AMS 5623B
CHEMICAL COMPOSITION (Mass weight - %)
C (％): 0.55 ~ 0.65
Si (％): ≤ 1.00
Mn (％): 5.00 ~ 6.00
P (％)≤: 0.035
S (％)≤: 0.025
Cr (％): -
Ni (％): 8.50 ~ 10.5
Mo (％): ≤ 0.50
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition: solution annealed
Tensile strength σb≥/MPa: 700
Yield strength σs≥/MPa: 300
Elongation δ5≥(%): 55.0
AKU≥/J: 300 min.
Hardness HBS: -
Condition: work hardened
Tensile strength σb≥/MPa: -
Yield strength σs≥/MPa: -
Elongation δ5≥(%): -
AKV≥/J: -
Hardness HBS: 149 ~ 179
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / AOD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - solution annealed treatment
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1