ASTM B511 Gr. N08330 Suppliers,China ASTM B511 Gr. N08330 Forging Bar plate machined, Ex-stock ASTM B511 Gr. N08330 Alloy Exporters - Technical specifications - ASTM A982 - 2015. From Melting, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic flaw detection test.
TECHNICAL DATA SHEET - ASTM B511 Grade N08330
TECHNICAL SPECIFICATIONS: ASTM B511 - 2016
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: This specification covers Stainless steel forgings for compressor and turbine bucket, blade, and airfoil applications.
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.08
Si (％): 0.75 ~ 1.50
Mn (％): ≤ 2.00
P (％) ≤: 0.030
S (％) ≤: 0.015
Cr (％): 17.0 ~ 20.0
Ni (％): 34.0 ~ 37.0
Cu (%): ≤ 1.00
Sn (%): ≤ 0.025
Pb (%): ≤ 0.005
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: This specification covers Stainless steel forgings for compressor and turbine bucket, blade, and airfoil applications.
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.08
Si (％): 0.75 ~ 1.50
Mn (％): ≤ 2.00
P (％) ≤: 0.030
S (％) ≤: 0.015
Cr (％): 17.0 ~ 20.0
Ni (％): 34.0 ~ 37.0
Cu (%): ≤ 1.00
Sn (%): ≤ 0.025
Pb (%): ≤ 0.005
Fe (%): Remainder
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/ ≥ MPa: 485
Yield strength, σ0.2/ ≥ MPa: 235
Elongation, δ (％) ≥: 30.0
Reduction of area, ф (％) ≥: -
Impact strength, AKv: -
Hardness ≤ (HBW): 255 Max.
HEAT TREATMENT PRACTICE
Condition: Quenched 1030 ~ 1050 Deg.C, oil or air cooling.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.5 ~ 600mm
Wire rod (Diameter): 3.0 ~ 13.0mm
Flat bar (width X thickness): 10 ~ 400 X 15 ~ 800mm
Length: random length, fixed length or based on the customer's special requirements.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/ ≥ MPa: 485
Yield strength, σ0.2/ ≥ MPa: 235
Elongation, δ (％) ≥: 30.0
Reduction of area, ф (％) ≥: -
Impact strength, AKv: -
Hardness ≤ (HBW): 255 Max.
HEAT TREATMENT PRACTICE
Condition: Quenched 1030 ~ 1050 Deg.C, oil or air cooling.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.5 ~ 600mm
Wire rod (Diameter): 3.0 ~ 13.0mm
Flat bar (width X thickness): 10 ~ 400 X 15 ~ 800mm
Length: random length, fixed length or based on the customer's special requirements.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Hot search：ASTM B511 Gr. N08330
Previous page：1.7020
Last page：ASTM A982 Gr.S41005
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1