ASTM A982 Grade C Blade Steel,ASTM A982 Grade C Suppliers,ASTM A982 Grade C Forging Bar plate machined, Ex-stock ASTM A982 Grade C Alloy Exporters, Technical specifications - ASTM A982 - 2015. From Melting, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic flaw detection test.
TECHNICAL DATA SHEET - ASTM A982 Grade C
TECHNICAL SPECIFICATIONS: ASTM A982 - 10 (2015)
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: This specification covers Stainless steel forgings for compressor and turbine bucket, blade, and airfoil applications.
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.10 ~ 0.17
Si (％): 0.10 ~ 0.35
Mn (％): 0.65 ~ 1.05
P (％) ≤: 0.020
S (％) ≤: 0.015
Cr (％): 11.25 ~ 12.75
Ni (％): 2.25 ~ 3.25
Mo (%): 1.50 ~ 2.00
N (%): 0.020 ~ 0.045
V (%): 0.25 ~ 0.40
W (%): ≤ 0.10
Al (%): ≤ 0.025
Nb (%): -
Co (%): -
Ti (%): ≤ 0.05
Cu (%): ≤ 0.15
Tin (%): ≤ 0.05
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/ ≥ MPa: 1000
Yield strength, σ0.2/ ≥ MPa: 795
Elongation, δ (％) ≥: 15.0
Reduction of area, ф (％) ≥: 30.0
Impact strength, AKv: 40J min.
Hardness ≤ (HBW): 352 Max.
HEAT TREATMENT PRACTICE
Condition: Quenched 995 ~ 1025 Deg.C, oil or air cooling, tempered 565 Deg.C Min, air cooling.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.5 ~ 600mm
Wire rod (Diameter): 3.0 ~ 13.0mm
Flat bar (width X thickness): 10 ~ 400 X 15 ~ 800mm
Length: random length, fixed length or based on the customer's special requirements.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: This specification covers Stainless steel forgings for compressor and turbine bucket, blade, and airfoil applications.
CHEMICAL COMPOSITION (WEIGHT %)
C (％): 0.10 ~ 0.17
Si (％): 0.10 ~ 0.35
Mn (％): 0.65 ~ 1.05
P (％) ≤: 0.020
S (％) ≤: 0.015
Cr (％): 11.25 ~ 12.75
Ni (％): 2.25 ~ 3.25
Mo (%): 1.50 ~ 2.00
N (%): 0.020 ~ 0.045
V (%): 0.25 ~ 0.40
W (%): ≤ 0.10
Al (%): ≤ 0.025
Nb (%): -
Co (%): -
Ti (%): ≤ 0.05
Cu (%): ≤ 0.15
Tin (%): ≤ 0.05
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/ ≥ MPa: 1000
Yield strength, σ0.2/ ≥ MPa: 795
Elongation, δ (％) ≥: 15.0
Reduction of area, ф (％) ≥: 30.0
Impact strength, AKv: 40J min.
Hardness ≤ (HBW): 352 Max.
HEAT TREATMENT PRACTICE
Condition: Quenched 995 ~ 1025 Deg.C, oil or air cooling, tempered 565 Deg.C Min, air cooling.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.5 ~ 600mm
Wire rod (Diameter): 3.0 ~ 13.0mm
Flat bar (width X thickness): 10 ~ 400 X 15 ~ 800mm
Length: random length, fixed length or based on the customer's special requirements.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Previous page：ASTM A982 Gr.S41005
Last page：ASTM B511 Gr.N08332
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1