ASTM A982 Gr.F
2020-05-27 09:05:08 Origin： Remark：0 Click：
ASTM A982 Gr.F Blade Steel, ASTM A982 Gr.F Suppliers, ASTM A982 Gr. Flat Bar plate machined, Ex-stock ASTM A982 Gr.F Alloy Exporters, Technical specifications - ASTM A982 - 2015. From Melting, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, Ultrasonic flaw detection test.
TECHNICAL DATA SHEET - ASTM A982 Grade F
TECHNICAL SPECIFICATIONS: ASTM A982 - 10 (2015)
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: This specification covers Stainless steel forgings for compressor and turbine bucket, blade, and airfoil applications.
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.70
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％) ≤: 0.030
S (％) ≤: 0.020
Cr (％): 15.0 ~ 17.5
Ni (％): 3.00 ~ 5.00
Mo (%): -
N (%): -
V (%): -
W (%): -
Al (%): -
Nb (%): 0.15 ~ 0.45
Co (%): -
Ti (%): -
Cu (%): 3.00 ~ 5.00
Tin (%): -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/ ≥ MPa: 935
Yield strength, σ0.2/ ≥ MPa: 725
Elongation, δ (％) ≥: 16.0
Reduction of area, ф (％) ≥: 50.0
Impact strength, AKv: 55J min.
Hardness ≤ (HBW): 341 Max.
HEAT TREATMENT PRACTICE
Condition: Quenched 1025 ~ 1050 Deg.C, oil or air cooling, aging 615 ~ 630 Deg.C Min, air cooling.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.5 ~ 600mm
Wire rod (Diameter): 3.0 ~ 13.0mm
Flat bar (width X thickness): 10 ~ 400 X 15 ~ 800mm
Length: random length, fixed length or based on the customer's special requirements.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: This specification covers Stainless steel forgings for compressor and turbine bucket, blade, and airfoil applications.
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.70
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％) ≤: 0.030
S (％) ≤: 0.020
Cr (％): 15.0 ~ 17.5
Ni (％): 3.00 ~ 5.00
Mo (%): -
N (%): -
V (%): -
W (%): -
Al (%): -
Nb (%): 0.15 ~ 0.45
Co (%): -
Ti (%): -
Cu (%): 3.00 ~ 5.00
Tin (%): -
MECHANICAL PROPERTY UNDER ROOM TEMP.
Tensile strength, σb/ ≥ MPa: 935
Yield strength, σ0.2/ ≥ MPa: 725
Elongation, δ (％) ≥: 16.0
Reduction of area, ф (％) ≥: 50.0
Impact strength, AKv: 55J min.
Hardness ≤ (HBW): 341 Max.
HEAT TREATMENT PRACTICE
Condition: Quenched 1025 ~ 1050 Deg.C, oil or air cooling, aging 615 ~ 630 Deg.C Min, air cooling.
MELTING PROCESS
The alloy is usually produced by BEF + AOD / EAF, followed by electroslag refining (ESR or VAR ) if necessary for special purpose.
PRODUCT FORMS AVAILABLE
Round bar (Diameter): 5.5 ~ 600mm
Wire rod (Diameter): 3.0 ~ 13.0mm
Flat bar (width X thickness): 10 ~ 400 X 15 ~ 800mm
Length: random length, fixed length or based on the customer's special requirements.
Form: wire or straightened bar
TECHNICAL SALES ASSISTANCE
If you meet further on any technical inquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Previous page：ASTM A982 Gr.S41041
Last page：ASTM A182 Gr.F304
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1