AISI 616 is a high content of 12.0% chromium martensitic alloy. Round bar S42200 Plate machined, 1.4935 Exporters - Technical standards - ASTM A565 or by agreement.
TECHNICAL DATA SHEET - Grade AISI 616
MATERIAL CATEGORY - High temperature martensitic high content chromium bars and forge piece
Stock available - Round bar diam. 20 ~ 300mm
CHEMICAL COMPOSITION (mass weight - %)
Carbon, C (％): 0.20 ~ 0.25
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 0.50 ~ 1.00
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 0.50 ~ 1.00
Molybdenum, Mo (％): 0.90 ~ 1.25
Tungsten, W (％): 0.90 ~ 1.25
Silicon, Si (％): ≤ 0.50
Manganese, Mn (％): 0.50 ~ 1.00
Phosphorus, P (％) ≤: 0.025
Sulfur, S (％) ≤: 0.015
Chromium, Cr (％): 11.0 ~ 12.5
Nickel, Ni (％): 0.50 ~ 1.00
Molybdenum, Mo (％): 0.90 ~ 1.25
Tungsten, W (％): 0.90 ~ 1.25
Vanadium, V (%): 0.20 ~ 0.30
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Condition of heat treatment: Annealed
Tensile strength, Rm ≥ MPa: -
Yield strength, Rp0.2 ≥ MPa:-
Yield strength, Rp0.2 ≥ MPa:-
Elongation, A ≥ (％): -
Reduction of area, Z ≥ (％): -
Hardness | HRS: ≤ 248
Reduction of area, Z ≥ (％): -
Hardness | HRS: ≤ 248
Condition of heat treatment: + T, middle tempered
Tensile strength, σb ≥/MPa: -
Yield strength, σ0.2 ≥/MPa:-
Yield strength, σ0.2 ≥/MPa:-
Elongation, δ ≥(％): -
Reduction of area, ф ≥(％): -
Hardness | HRS: ≤ 285
Reduction of area, ф ≥(％): -
Hardness | HRS: ≤ 285
Condition of heat treatment: HT 1022℃ ~ 1050℃ air or oil cooled, ≥620℃ X 2H, tempered
Tensile strength, σb ≥/MPa: 965
Yield strength, σ0.2 ≥/MPa: 760
Yield strength, σ0.2 ≥/MPa: 760
Elongation, δ ≥(％): 13.0
Reduction of area, ф ≥(％): 30.0
Hardness | HRS: 302 ~ 352
Reduction of area, ф ≥(％): 30.0
Hardness | HRS: 302 ~ 352
Condition of heat treatment: H 1022℃ ~ 1050℃ air or oil cooled, ≥677℃ X 2H, tempered
Tensile strength, σb ≥/MPa: 825
Yield strength, σ0.2 ≥/MPa: 585
Yield strength, σ0.2 ≥/MPa: 585
Elongation, δ ≥(％): 17.0
Reduction of area, ф ≥(％): 35.0
Hardness | HRS: 241 ~ 285
Reduction of area, ф ≥(％): 35.0
Hardness | HRS: 241 ~ 285
PRODUCT DESCRIPTION
The alloy is usually produced by BEF / EAF + VD +LF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered + SRA
The alloy is usually produced by BEF / EAF + VD +LF followed by electroslag refining (ESR) / VAR if necessary for special purpose. Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the annealed condition.
Final heat treatment - Quenched and tempered + SRA
PRODUCT PROFILE AND DIMENSIONS
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 5.5mm to 550mm
Square bar / Flat bar: 10mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Heavy/middle plate via hot rolled: T60 - 400mm X W60 ~ 1000mm X L1000 ~ 5000mm
Forging piece: stepped shafts, other different shapes based on OEM.
Forging piece: stepped shafts, other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our resident team of qualified production engineers.
Previous page：STR 310
Last page：ASTM A182 Gr.F304L
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1