N06693 datasheet, N06693 Chemical compositions, N06693 Properties from Steelmaking, ESR & VAR technique, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
TECHNICAL DATA SHEET - Grade Inconel 693 & N06693
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Nickel base Superalloy
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.15
Si (％): ≤ 0.50
Mn (％): ≤ 1.00
P (％) ≤: 0.035
S (％) ≤: 0.010
Cr (％): 27.0 ~ 31.0
Ni (％): Balance
Si (％): ≤ 0.50
Mn (％): ≤ 1.00
P (％) ≤: 0.035
S (％) ≤: 0.010
Cr (％): 27.0 ~ 31.0
Ni (％): Balance
Mo (%): -
Co (％): -
W (%): -
Al (%): 2.50 ~ 4.00
Cu (%): ≤ 0.50
Ti (%): ≤ 1.00
Nb/Ta (%): 0.50 ~ 2.50
Fe (%): 2.50 ~ 6.00
TYPICAL MECHANICAL PROPERTIES UNDER SOLUTION ANNEALED
Tensile strength, σb/≥ MPa: 690
Yield strength, σ0.2/MPa: 345
Elongation, δ ≥(％): 30.0
Reduction of area, ф ≥ (％): -
Hardness via heat treatment /HBW: -
Reduction of area, ф ≥ (％): -
Hardness via heat treatment /HBW: -
TYPICAL APPLICATIONS
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged or Double aged.
AVAILABLE FORMS AND SHAPES
Round bar (Diameter): 5.50 ~ 450mm
Square bar / Flat bar: 3 ~ 350mm
Superalloy is widely used to produce the high temperature components for gas turbine in the field of aviation, naval vessels and industry, such as turbine blade, guide blade, turbine disc, high pressure compressor disc, combustor, and also production of energy conversion devices, such as aerospace craft, rocket motor, nuclear reactor, petrochemical equipments, coaly transforming and so on. The alloy is usually produced by AOD / VOD /VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied bright surface in the solution annealed condition.
Final heat treatment - solution + Aged or Double aged.
AVAILABLE FORMS AND SHAPES
Round bar (Diameter): 5.50 ~ 450mm
Square bar / Flat bar: 3 ~ 350mm
Wire rod (Diameter): 0.10 ~ 16mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form)
Forging piece: Different shapes based on OEM.
Other sizes can be supplied to meet specific requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers.
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers.
Hot search：N06693
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1