J91631 Ex-stock, Steel Coils J91631 Chemical, S41800 Strip forging Bar rod steelmaking, ESR, Blooming, Hot forging & Rolling, Heat treatment, Straightened, Ultrasonic test, Cold working, Machined. We also possess advanced precision machining equipments for further processing.
TECHNICAL SPECIFICATION DATASHEET - UNS J91631
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: Martensitic high content chromium round bar and forge piece
MATERIAL SPECIFICATIONS: ASTM A565
CHEMICAL COMPOSITION (WEIGHT %)
C (%): 0.15 ~ 0.20
Si (%): ≤ 0.50
Mn (%): ≤ 0.50
P (%)≤: 0.040
S (%)≤: 0.030
Cr (%): 12.0 ~ 14.0
Ni (%): 1.80 ~ 2.20
Mo (%): ≤ 0.50
W (%): 2.50 ~ 3.50
Si (%): ≤ 0.50
Mn (%): ≤ 0.50
P (%)≤: 0.040
S (%)≤: 0.030
Cr (%): 12.0 ~ 14.0
Ni (%): 1.80 ~ 2.20
Mo (%): ≤ 0.50
W (%): 2.50 ~ 3.50
MECHANICAL PROPERTIES UNDER DIFFERENT HEAT TREATMENT
Condition of heat treatment: Annealed
Tensile strength, σb ≥/MPa: -
Yield strength, σ0.2 ≥/MPa:-
Yield strength, σ0.2 ≥/MPa:-
Elongation, δ ≥(%): -
Reduction of area, ф ≥(%): -
Hardness | HBW: ≤ 311
Reduction of area, ф ≥(%): -
Hardness | HBW: ≤ 311
Condition of heat treatment: HT 981℃ ~ 1080℃ air or oil cooled, ≥620℃ X 2H, two times tempered
Tensile strength, σb ≥/MPa: 965
Yield strength, σ0.2 ≥/MPa: 760
Yield strength, σ0.2 ≥/MPa: 760
Elongation, δ ≥(%): 15.0
Reduction of area, ф ≥(%): 45.0
Hardness | HBW: 302 ~ 352
Reduction of area, ф ≥(%): 45.0
Hardness | HBW: 302 ~ 352
PRODUCT DESCRIPTION
The alloy is usually produced by BEF + AOD / VD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black / bright in the annealed condition.
Final heat treatment - Quenched and Tempered
The alloy is usually produced by BEF + AOD / VD / EAF followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black / bright in the annealed condition.
Final heat treatment - Quenched and Tempered
PRODUCT PROFILE
Round bar / Wire rod (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Round bar / Wire rod (Diameter): 5.5mm to 600mm
Square bar / Flat bar: 3mm to 800mm
Length: Fixed length or random length or based on the customer's special requirement.
Steel strip via cold rolled: T0.5 - 3mm X W5 - 300mm X L (or in coil form)
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
Forging piece: stepped shafts with flanks / discs /tubes /slugs /donuts /cubes /other different shapes based on OEM.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
If you meet further on any technical enquiry, pleased to EMAIL our resident team of qualified production engineers. E-mail: sales@ccsteels.com
Hot search:J91631
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1