Z5CNU15-05
2020-07-21 09:24:45 Origin： Remark：0 Click：
Descriptions Z5CNU15-05 datasheet,Z5CNU15-05 Chemical,Z5CNU15-05 Properties Steelmaking, Blooming, Hot forging, Hot rolling, Heat treatment, Straightening, 100% Ultrasonic flaw detection test, Cold working or Machined. All of these materials conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
STAINLESS STEEL DATA SHEET - Grade Z5CNU15-05
OFFICIAL TEST CERTIFICATE: issued by TUV - SGS - BV
MATERIAL CATEGORY: 15Cr - 5Ni - 4Cu Martensitic stainless
CHEMICAL COMPOSITION (WEIGHT %)
C (％): ≤ 0.07
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 14.0 ~ 15.5
Ni (％): 3.50 ~ 5.50
Mo (％): —
Si (％): ≤ 1.00
Mn (％): ≤ 1.00
P (％)≤: 0.040
S (％)≤: 0.030
Cr (％): 14.0 ~ 15.5
Ni (％): 3.50 ~ 5.50
Mo (％): —
Cu (％): 2.50 ~ 4.50
Nb+Ta (%): 0.15 ~ 0.45
MECHANICAL PROPERTIES UNDER ROOM TEMP.
Form: Bar, forge piece
Condition: H900
Tensile strength, σb/MPa: 1310
Yield strength, σ0.2/MPa: 1170
Elongation, δ (％): 10.0
Reduction of area, ψ (％): 35
Harndess: HRC: ≥ 40
Condition: H900
Tensile strength, σb/MPa: 1310
Yield strength, σ0.2/MPa: 1170
Elongation, δ (％): 10.0
Reduction of area, ψ (％): 35
Harndess: HRC: ≥ 40
Form: Bar, forge piece
Condition: H925
Condition: H925
Tensile strength, σb/MPa: 1170
Yield strength, σ0.2/MPa: 1070
Elongation, δ (％): L-10.0
Reduction of area, ψ (％): L-38.0
Hardness HRC: ≥ 38
Yield strength, σ0.2/MPa: 1070
Elongation, δ (％): L-10.0
Reduction of area, ψ (％): L-38.0
Hardness HRC: ≥ 38
Form: Bar, forge piece
Condition: H1025
Condition: H1025
σb/MPa: 1070
σ0.2/MPa: 1000
δ (％): 12.0
σ0.2/MPa: 1000
δ (％): 12.0
ψ (％): 45
Hardness HRC: ≥ 35
Hardness HRC: ≥ 35
Form: Bar, forge piece
Condition: H1075
Condition: H1075
σb/MPa: 1000
σ0.2/MPa: 860
δ (％): 13.0
σ0.2/MPa: 860
δ (％): 13.0
ψ (％): 45.0
Hardness HRC: ≥32
Hardness HRC: ≥32
Form: Bar, forge piece
Condition: H1100
Condition: H1100
σb/MPa: 965
σ0.2/MPa: 795
δ(％): 14；10
ψ(％): 45；29
HRC: ≥31
σ0.2/MPa: 795
δ(％): 14；10
ψ(％): 45；29
HRC: ≥31
PRODUCT DESCRIPTION
The alloy is usually produced by AOD / VD / VIM followed by electroslag refining (ESR) / VAR if necessary for special purpose.
Bars and, where applicable, forgings are subjected to ultrasonic examination based on the different levels according to the buyers' requirements.
Bars are usually supplied black/bright in the softened condition.
Final heat treatment - solution treatment + A
TYPICAL APPLICATIONS
Chemical equipment
Mechanical parts used in the condition of corrosion resistance
Bolts and nuts
Pressure vessel
AVAILABLE FORMS AND SHAPES
Round bar (Diameter): 5.5 ~ 550mm
Square bar / Flat bar: 3 ~ 350mm
AVAILABLE FORMS AND SHAPES
Round bar (Diameter): 5.5 ~ 550mm
Square bar / Flat bar: 3 ~ 350mm
Rolled plate: 10 ~ 400 X 60 ~ 1200 X length
Wire rod (Diameter): 0.10 ~ 16mm
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form).
Forging piece: Different shapes based on OEM.
Steel strip via cold rolled: T0.1 - 3mm X W5 - 650mm X L (or in coil form).
Forging piece: Different shapes based on OEM.
Other sizes can be supplied to meet specific requirements.
TECHNICAL SALES ASSISTANCE
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers.
If you meet further on any technical enquiry, pleased to EMAIL (sales@ccsteels.com) our qualified production engineers.
Hot search：Z5CNU15-05
Previous page：ASTM A182 Gr.F310
Last page：Z5CNU15.05
Total list
Monthly rank
- 24X35CrMo17
- 23Z15CN17-03
- 23ASTM A565 Gr.616HT
- 21X10CrNiW17-13-3
- 19ASTM A638 Gr.660
- 18AISI 306
- 15SAE 51420
- 14P550
- 14SAE 51416
- 14X12CrMoWVNbN10-1-1